| Journal: | Superficies y vacío |
| Database: | PERIÓDICA |
| System number: | 000368104 |
| ISSN: | 1665-3521 |
| Authors: | Martínez Ceballos, E. C Vera Graziano, R1 Martínez Barrera, G2 Olea Mejía, O2 |
| Institutions: | 1Universidad Nacional Autónoma de México, Instituto de Investigación en Materiales, México, Distrito Federal. México 2Universidad Autónoma del Estado de México, Facultad de Química, Toluca, Estado de México. México |
| Year: | 2012 |
| Season: | Mar |
| Volumen: | 25 |
| Number: | 1 |
| Country: | México |
| Language: | Español |
| Document type: | Artículo |
| Approach: | Experimental, aplicado |
| Spanish abstract | Un problema de suma importancia en las resinas dentales poliméricas, es el efecto que causa su contracción cuando se polimeriza in–situ. Esta contracción disminuye la efectividad del implante ya que cuando la resina endurece y se adhiere al diente se generan fisuras y otros defectos que permiten la absorción de alimentos y la formación de caries. Esta contracción también disminuye las propiedades mecánicas de la resina implantada. Para disminuir la contracción por polimerización y evitar estos problemas, se puede modificar la estructura química de la resina y de otros componentes. En este trabajo se reportan las características de una resina fotopolimerizable de Bis–GMA/TEGDMA modificada con poli[bis(2–hidroxietilmetacrilato)–fosfaceno] y poli[bis(2–hidroxietilmetacrilato)–injerto–poli(ácido láctico)–fosfaceno] a diferentes concentraciones. Se analizó el intervalo de contracción mediante el método conocido como "bonded–disk". Los valores obtenidos para el composito varían entre 5.3 y 3.8%; mientras que la velocidad de contracción de polimerización se encontró entre 82.7 y 60.1 µm/mín. El análisis mostró que al incorporar una mayor cantidad de dobles ligaduras se obtiene un menor porcentaje de encogimiento |
| English abstract | One of the most important problems on dental polymeric resins is the polymerization shrinkage effect caused by the in–situ in teeth. Resin shrinkage decreases the performance of the implant because after resin hardening and adhesion to teeth fissures and other defects are formed. These defects lead to microleakage and caries and also affect the mechanical properties. In order to reduce polymerization shrinkage and avoid these problems the chemical structure of the resin and other components are modified. The characteristics of light cured Bis–GMA/TEGDMA resin modified with poly[bis(2–hydroxy ethyl methacrylate)–phosphazene] and poly[(2–hydroxyethylmethacrylate)–graft–poly(lactic acid)]phosphazene at different concentrations are reported here. The contraction range was studied by the bonded–disk method. Total shrinkage–strain of the photo–polimerized resins varied between 5.3 y 3.8% while the contraction rate occurred between 82.7 and 60.1 µm/min. This analysis showed that polymerization shrinkage decreased in inverse proportion to the double bonds present in the resin |
| Disciplines: | Ingeniería, Medicina |
| Keyword: | Ingeniería de materiales, Odontología, Materiales dentales, Resinas, Metacrilato, Polifosfacenos, Polimerización, Encogimiento |
| Keyword: | Engineering, Medicine, Materials engineering, Dentistry, Dental materials, Resins, Methacrylate, Polyphosphazenes, Polymerization, Shrinkage |
| Full text: | Texto completo (Ver HTML) |