| Journal: | Journal of the Mexican Chemical Society |
| Database: | PERIÓDICA |
| System number: | 000447259 |
| ISSN: | 1870-249X |
| Authors: | Adeel, Shahid1 Kiran, Shumaila2 Jannat, Maria2 Amin, Nimra2 Hassan, Atya3 Qayyum, Muhammad Abdul4 Khan, Shahid Rehman5 |
| Institutions: | 1Government College University, Department of Chemistry, Faisalabad. Pakistán 2Government College University, Department of Applied Chemistry, Faisalabad. Pakistán 3Federal Urdu University of Arts, Department of Chemistry, Karachi, Baluchistán. Pakistán 4University of Education, Division of Science & Technology, Lahore, Punjab. Pakistán 5Applied Chemistry Research Centre, Laboratories Complex Ferozepur Road, Lahore, Punjab. Pakistán |
| Year: | 2021 |
| Season: | Jul-Sep |
| Volumen: | 65 |
| Number: | 3 |
| Pages: | 396-404 |
| Country: | México |
| Language: | Inglés |
| Document type: | Artículo |
| Approach: | Experimental, analítico |
| Spanish abstract | La radiación ultrasónica (U:S. por sus siglas en inglés) es la tecnología sostenible y verde que ha transformado el campo de los textiles. En este estudio, se llevó a cabo un tratamiento ultrasónico para mejorar el teñido reactivo de tela celulósica por el tinte Violet H3R. Para este propósito, se llevó a cabo un tratamiento con ultrasonido tanto a la solución como a la tela por hasta 60 minutos a 30 y 60 oC. Se obtuvieron resultados prometedores cuando la tela celulósica se expuso a un tratamiento con ultrasonido a 50 oC durante un período de 30 min, utilizando un baño de tinte (de 55 mL) a pH 7,5 de sal de Glauber (8 g/L). Estas condiciones representan un sistema de agotamiento, aplicado a 60 oC durante 55 min. Se obtuvieron varios tonos de tela de algodón teñidos en condiciones óptimas, lo que mostró que el tratamiento por ultrasonido mejora no solo la intensidad del color sino también el índice de solidez de media a sobresaliente. Por lo tanto, del estudio actual se puede concluir que el tratamiento con ultrasonido no solo es lo suficientemente bueno para mejorar la capacidad de teñido del tinte Reactive Violet H3R, sino que también realza las características del color de la tela de algodón teñida |
| English abstract | Ultrasonic radiation (U. S.) is the sustainable and green technology which has transformed the domain of textiles. In the current study, ultrasonic treatment was employed to improve the reactive dyeing of cellulosic fabricby Violet H3R dye. For this purpose, U.S. treatment has been given to both solution & fabric upto 50 min. at 30 to 60 oC. Promising results were obtained when cellulosic fabric was exposed to U.S. treatment at at 50 oC for a period of 30 min. using dye bath of 55 mL having 7.5 pH. Glauber salt (8 g/L) was employed as an exhausting agent at 60 oC for 55 min. Various shades of cotton fabric dyed at optimal conditions were obtained which showed that U.S. treatment has enhanced not only the colour strength but also the fastness rating from medium to outstanding. So, it can be concluded from the current study that U. S. treatment is not only good enough for improving the dyeing aptitude of Reactive Violet H3R dye, but it also uplifts the color features of dyed cotton fabric |
| Disciplines: | Química |
| Keyword: | Química industrial, Industria textil, Fibras de celulosa, FTIR, Colorantes, SEM, Radiación ultrasónica |
| Keyword: | Industrial chemistry, Textile industry, Cellulose fibers, FTIR, Dyes, SEM, Ultrasonic irradiation |
| Full text: | Texto completo (Ver HTML) Texto completo (Ver PDF) |