Determination of Phase Transition by Principal Component Analysis Applied to Raman Spectra of Polycristalline BATIO3 at Low and High Temperature



Document title: Determination of Phase Transition by Principal Component Analysis Applied to Raman Spectra of Polycristalline BATIO3 at Low and High Temperature
Journal: Journal of applied research and technology
Database: PERIÓDICA
System number: 000366203
ISSN: 1665-6423
Authors: 1
1
2
1
1
Institutions: 1Universidad Nacional Autónoma de México, Centro de Ciencias Aplicadas y Desarrollo Tecnológico, México, Distrito Federal. México
2Universidad Nacional Autónoma de México, Instituto de Ingeniería, México, Distrito Federal. México
Year:
Season: Feb
Volumen: 10
Number: 1
Pages: 57-62
Country: México
Language: Inglés
Document type: Artículo
Approach: Experimental, aplicado
Spanish abstract Este trabajo describe el análisis de las componentes principales (PCA) aplicados a los espectros Raman del BaTiO3 como función de la temperatura. Durante el experimento las muestras fueron calentadas continuamente y los espectros Raman fueron registrados cada 0.5 °C a una razón de 0.1 °C por minuto. Este procedimiento es aplicado para muestras de polvo compacto de BaTiO3 para obtener su comportamiento térmico de –190 °C a 230 °C. La técnica del PCA fue capaz de distinguir características espectrales para determinar la temperatura de la transición de fase y la historia térmica completa, incluyendo las transiciones de fase estructural: romboédrica a ortorrómbica at –100 °C, ortorrómbica a tetragonal at –5°C y tetragonal a cúbica at 121 °C
English abstract This work describes the principal component analysis (PCA) applied to Raman spectra of polycrystalline BaTiO3 as a function of temperature. During each experiment the samples was continuously heated and the Raman spectrum was registered every 0.5 °C at a rate of 0.1 °C min–1. This procedure is applied on samples BaTiO3 compact powder to obtain their thermal behavior from –190 °C to 230 °C. The PCA method was able to distinguish spectral features to determine the phase transition temperature and the whole thermal history including the structural phase transition from rhombohedra to orthorhombic at –100 °C, orthorhombic to tetragonal at –5 °C and tetragonal to cubic at 121 °C
Disciplines: Ingeniería
Keyword: Ingeniería de materiales,
Trióxido de titanio-bario,
Transición de fase,
Espectroscopía Raman,
Análisis de componentes principales
Keyword: Engineering,
Materials engineering,
Barium-titanium trioxide,
Phase transition,
Principal component analysis,
Raman spectroscopy
Full text: Texto completo (Ver HTML)