| Journal: | Facultad de Ingeniería - Universidad Pedagógica y Tecnológica de Colombia |
| Database: | PERIÓDICA |
| System number: | 000441652 |
| ISSN: | 0121-1129 |
| Authors: | Socarrás Cordoví, Yamila Concepción1 González Díaz, Liliana1 Alvarez Deulofeu, Eduardo1 González Fernández, Mayra1 Roca Fernández, Estrella1 Torres Shoembert, Raúl1 |
| Institutions: | 1Universidad de Oriente, Santiago de Cuba. Cuba |
| Year: | 2020 |
| Season: | Ene-Mar |
| Volumen: | 29 |
| Number: | 54 |
| Country: | Colombia |
| Language: | Inglés |
| Document type: | Artículo |
| Approach: | Aplicado, descriptivo |
| Spanish abstract | Se valora la durabilidad del hormigón del sistema prefabricado Gran Panel Soviético, a través de la precisión de la resistencia a compresión, la velocidad del pulso ultrasónico y el índice esclerométrico. Igualmente, se determinan otros parámetros como la humedad y el potencial de corrosión, que también inciden en la durabilidad del hormigón. Se recurre esencialmente a métodos experimentales y estadísticos, no obstante, se emplean métodos como el histórico-lógico y técnicas como las encuestas y entrevistas, para recopilar mayor cantidad de información sobre la resistencia a compresión de los elementos prefabricados en el proyecto original. Al analizar los resultados se concluye que, en los elementos en buen estado técnico-constructivo, que conforman las edificaciones en explotación, el hormigón es de resistencia media al igual que lo prescribe el proyecto original de este sistema prefabricado. Sin embargo, en los elementos con presencia de daños patológicos la resistencia es baja. Debido a que en estos elementos se evidencian procesos de deterioro químico, causado por el ataque del agua, que generan formación de compuestos solubles de la pasta, la pérdida de masa y la disminución de resistencia mecánica entre otras alteraciones. A la par se desencadena la carbonatación del hormigón, que provoca a su vez la corrosión del acero de refuerzo. Esta corrosión conduce al agrietamiento del hormigón, delaminación del acero, disminución de la adherencia hormigón-acero y demás manifestaciones, que afectan la durabilidad del hormigón. Por lo tanto, se debe valorar la incidencia de la durabilidad del hormigón, en el comportamiento sismorresistente de estas edificaciones |
| English abstract | The durability of the concrete of the precast Great Soviet Panel system is valued through the resistance to compression, ultrasonic pulse velocity, surface methods, humidity and potential of corrosion. The evaluation is approached, essentially, through experimental and statistical methods, nevertheless, historical-logical and technical methods, such as surveys and interviews, are used in order to gather a bigger amount of information on the resistance to compression of the elements in the original project. While analyzing the results, we can conclude that, in elements in a good technical-constructive state that conform the constructions in exploitation, concrete has an average resistance. However, in elements with the presence of pathological damages, the resistance is low due to the fact that elements show chemical deterioration processes caused by water exposure, which generates the formation of soluble paste compounds, loss of mass, and decrease in mechanical resistance, among other alterations. At the same time, carbonation of concrete is triggered, which, in turn, causes the corrosion of the reinforcing steel. This corrosion leads to the cracking of concrete, delamination of steel, decrease of the concrete-steel adhesion, and other manifestations that affect the durability of concrete. Therefore, the incidence of the durability of concrete should be valued in the structural seismic behavior of constructions |
| Portuguese abstract | Valora-se a durabilidade do concreto do sistema pré-fabricado Grande Painel Soviético, através da precisão da resistência à compressão, à velocidade do pulso ultrassônico e ao índice esclerométrico. Igualmente, determinam-se outros parâmetros como a humidade e o potencial de corrosão, que também incidem na durabilidade do concreto. Recorre-se essencialmente a métodos experimentais e estatísticos, mesmo assim, empregam-se métodos como o histórico-lógico e técnicas como as enquetes e entrevistas, para recopilar maior quantidade de informação sobre a resistência à compressão dos elementos pré-fabricados no projeto original. Ao analisar os resultados conclui-se que, nos elementos em bom estado técnico-construtivo, que conformam as edificações em exploração, o concreto é de resistência média ao igual que o prescreve o projeto original deste sistema pré-fabricado. Porém, nos elementos com presença de danos patológicos, a resistência é baixa. Devido a que nestes elementos evidenciam-se processos de deterioro químico, causado pelo ataque de água, que geram formação de compostos solúveis da pasta, a perda de massa e a diminuição de resistência mecânica, entre outras alterações. Juntamente, desencadeia-se a carbonatação do concreto, que provoca por sua vez, a corrosão do aço de reforço. Esta corrosão conduz à fissuração do concreto, delaminação do aço, diminuição da aderência concreto-aço e demais manifestações, que afetam a durabilidade do concreto. Portanto, deve-se valorar a incidência da durabilidade do concreto, no comportamento sismorresistente destas edificações |
| Disciplines: | Ingeniería |
| Keyword: | Ingeniería civil, Materiales de construcción, Concreto prefabricado, Índice esclerométrico, Porcentaje de humedad, Potencial de corrosión, Resistencia a compresión, Velocidad del pulso ultrasónico |
| Keyword: | Civil engineering, Construction materials, Precast concrete, Compression resistance, Humidity percentage, Potential of corrosion, Surface methods, Ultrasonic pulse velocity |
| Full text: | Texto completo (Ver HTML) Texto completo (Ver PDF) |