| Revue: | Revista mexicana de física |
| Base de datos: | PERIÓDICA |
| Número de sistema: | 000327717 |
| ISSN: | 0035-001X |
| Autores: | Parra–Arciniega, S.M. de la1 Alvarez–Méndez, A1 Torres–González, L.C1 Sánchez, E.M1 |
| Instituciones: | 1Universidad Autónoma de Nuevo León, Monterrey, Nuevo León. México |
| Año: | 2009 |
| Periodo: | Feb |
| Volumen: | 55 |
| Número: | 1 |
| Paginación: | 32-37 |
| País: | México |
| Idioma: | Inglés |
| Tipo de documento: | Artículo |
| Enfoque: | Experimental |
| Resumen en español | Estudios realizados en el sistema vítreo Na2O–CaO–3SiO2 sugieren que su transformación de fase ocurre desde su superficie hacia su interior. En estudios previos realizados se reportó la modificación del mecanismo de cristalización por adición de agentes nucleantes. En este estudio partículas nanometricas de TiO2 fueron adicionadas con la idea de modificar el mecanismo de cristalización. Los vidrios obtenidos así como muestras tratadas térmicamente fueron evaluadas por difracción de rayos–X, análisis térmico diferencial, microscopía óptica y de transmisión electrónica de alta resolución. El rango de estudio realizado fue de 0–10 % en peso y se encontró que en la máxima adición se disminuyó considerablemente el proceso de cristalización. A pesar de la rápida disolución lograda por la adición de nanopartículas de titania no se logró un cambio del proceso de cristalización |
| Resumen en inglés | Studies conducted into Na2O–CaO–3SiO2 glass composition suggest that its phase transformation occurs from the surface towards the interior of the sample. In a study carried out in 1982, it was reported that no addition of nucleating agents modified the mechanism. Taking advantage of the disposition materials synthesized by nanotechnology, in this study TiO2 in nanometer size was used with the idea that, because of its qualities, it could modify the crystallization mechanism. The glasses obtained as well as the thermally treated samples, were evaluated by the X–ray diffraction (XRD) powder method, differential thermal analysis (DTA), and by optical microscopy and high resolution transmission electron microscopy (HRTEM). Within the range of TiO2 concentration studied (0 – 10 wt %), 10 wt % of TiO2 considerably reduced the Na2O–2CaO–3SiO2 phase crystallization process. The crystallization mechanism was not modified and TiO2 did not form compounds with the matrix components |
| Disciplinas: | Física y astronomía, Química |
| Palabras clave: | Física de materia condensada, Termodinámica y física estadística, Química inorgánica, Estado sólido, Vidrio calizo, Cristalización, Difracción de rayos X, Análisis térmico diferencial, Microscopía |
| Keyword: | Physics and astronomy, Chemistry, Condensed matter physics, Thermodynamics and statistical physics, Inorganic chemistry, Glass, Crystallization, Diffraction-x rays, Differential thermal analysis, Microscopy |
| Texte intégral: | Texto completo (Ver HTML) |