| Revue: | CienciAmérica |
| Base de datos: | PERIÓDICA |
| Número de sistema: | 000426108 |
| ISSN: | 1390-681X |
| Autores: | Nicolalde, Juan Francisco1 Martínez Gómez, Javier1 Avila, Alvaro2 Maiguashca, Javier3 |
| Instituciones: | 1Universidad Internacional SEK, Facultad de Arquitectura e Ingeniería, Quito, Pichincha. Ecuador 2Instituto Nacional de Eficiencia Energética y Energías Renovables, Centro de Investigación, Quito, Pichincha. Ecuador 3Instituto Espacial Ecuatoriano, Centro de Investigación, Quito, Pichincha. Ecuador |
| Año: | 2019 |
| Periodo: | Ene-Jun |
| Volumen: | 8 |
| Número: | 1 |
| Paginación: | 105-119 |
| País: | Ecuador |
| Idioma: | Español |
| Tipo de documento: | Artículo |
| Enfoque: | Aplicado, analítico |
| Resumen en español | El refuerzo de resinas con fibras naturales es utilizado a nivel mundial y debido a la biodiversidad del Ecuador sus fibras de origen natural supondrían un aporte a la manufactura de partes como materiales compuestos. OBJETIVO. Caracterizar la fibra de mocora como refuerzo de resina poliéster insaturada, determinarlas propiedades del material y encontrar la viabilidad de aplicaciones en el área mecánica. MÉTODO. Esta investigación comienza con el levantamiento y documentación de información de la fibra. Caracterización de la fibra tomando medidas, realizando microscopia, SEM, análisis de absorción de humedad, observación de la reacción de la fibra ante la resina, caracterización mecánica del material compuesto,diseñando moldes para probetas y pruebas mecánicas en base anormas ASTM. RESULTADOS. Se demuestra que la fibra tiene distintas longitudes enorientaciones 90º con un recubrimiento, la fibra tiene capas impermeables y surcos internos, tiene una absorción de humedad promedio de 61%, el molde de madera resiste la presión, hay encapsulación de la fibra, pero no tiene mojabilidad con la resina poliéster DISCUSIÓN Y CONCLUSIONES. El molde obtiene probetas sin derramamientos, pero la fibra esinviable como material compuesto bajo las condiciones naturales, sugiriendo futuras investigaciones con tratamientos enzimáticos a la fibra |
| Resumen en inglés | The reinforcement of resins with natural fibers is used worldwide and due to the biodiversity of Ecuadorit’snaturaloriginfibers would suppose a contribution to the manufacture of parts as composite materials. OBJECTIVE. Characterize the mocora fiber as reinforcement of unsaturated polyester resin, determine the properties of the material and find theviability ofapplications in the mechanical area. METHOD. This research begins with the collection and documentation of fiber information. Characterization of the fiber taking measurements, performing microscopy, SEM, analysis of moisture absorption, observation of the reaction of the fiber with the resin, mechanical characterization of the composite material, designing molds for test pieces and mechanical tests based on ASTM standards. RESULTS.It is shown that the fiber has different lengths in 90º orientations with a coating, the fiber has impermeable layers and internal grooves, has an average moisture absorption of 61%, the wood mold resists the pressure, there is encapsulation of the fiber, but It hasn’twettability with polyester resin. DISCUSSION AND CONCLUSIONS.The mold obtains samples without spills, but the fiber is unfeasible as a composite material under natural conditions, suggesting future investigations with enzymatic treatments to the fiber |
| Resumen en portugués | O reforço de resinas com fibras naturais é usado em todo o mundo e, devido à biodiversidade do Equador, seufibrasde origemnaturalsupõem uma contribuição para a fabricação de peças como materiais compostos. OBJETIVO.Caracterizar a fibra mocora como reforço de resina de poliéster insaturado, determinar as propriedades do material e encontrar a viabilidade de aplicações na área mecânica. MÉTODO.Esta pesquisa começa com a coleta e documentação de informações de fibra. Caracterização dasmedidas de tomada de fibra, realização de microscopia, MEV, análise de absorção de umidade, observação da reação da fibra antes da resina, caracterização mecânica do material compósito, desenho de moldes para peças de teste e ensaios mecânicos baseados empadrões ASTM. RESULTADOS.É mostrado que a fibra tem diferentes comprimentos em orientações de 90º com um revestimento, a fibra possui camadas impermeáveis e sulcos internos, tem uma absorção média de 61%, o molde de madeira resiste à pressão, há encapsulamento da fibra, mas não Tem molhabilidade com resina de poliéster DISCUSSÃO E CONCLUSÕES. O bolor obtém amostras sem derrames, mas a fibra é inviável como material compósito sob condições naturais, sugerindo futuras investigações com tratamentos enzimáticos para a fibra |
| Disciplinas: | Ingeniería |
| Palabras clave: | Ingeniería de materiales, Ingeniería mecánica, Compuestos, Mocora, Poliéster, SEM, Simulación |
| Keyword: | Materials engineering, Mechanical engineering, Compounds, Mocora, Polyester, SEM, Simulation |
| Texte intégral: | Texto completo (Ver HTML) |