| Journal: | Revista técnica de la Facultad de Ingeniería. Universidad del Zulia |
| Database: | PERIÓDICA |
| System number: | 000349955 |
| ISSN: | 0254-0770 |
| Authors: | Sánchez, Miguel1 Contreras, Ramón1 Pérez, Orlando1 Rincón, Oladis de1 Campos, William1 |
| Institutions: | 1Universidad del Zulia, Centro de Estudios de Corrosión, Maracaibo, Zulia. Venezuela |
| Year: | 2007 |
| Volumen: | 30 |
| Pages: | 188-197 |
| Country: | Venezuela |
| Language: | Español |
| Document type: | Conferencia o discurso |
| Approach: | Aplicado, descriptivo |
| Spanish abstract | En este trabajo se presentan los resultados de la evaluación de probetas de acero galvanizado por irmersión en caliente con tiempo de baño de 1.2 y 3 minutos. Se realizaron ensayos de espesor de recubnmiento y mediante técnicas electroquímicas se midió la velocidad de corrosión del acero en soluciones de baños ácidos a 5; 10 y 16% de HCl y agua de enjuage pH 2.50; 3,50 y 4,50; y del acero galvanizado en una solución de NaCl3.5Oh. Se analizaron ciertos parámetros operacionales, tales como el envejecimiento del baño ácido (HCl), y eliminación de la etapa de enjuague, para observar su influencia en el recubrimiento de cinc. Se encontró que a medida que aumenta rl espesor del recubrimiento disminuye la velocidad de corrosion. Mediante el uso del microscopio electrónico de bamdo se determinó que cuando se obvia el enjuague, el cloro puede quedar atrapado cntre dos capas (interfase). y luego migra de la capa superior (Delta) hacia la inferior (Gamma) |
| English abstract | An evaluation by hot dip galvanizing on steel after a 1; 2 and 3-minutes immersion was studied. These samples were carried out for evaluating microhardness and thickness measurements. Electrochemical techniques were used to determined the corrosion rate of steel in acid pickling 5; 10 and 16% HC1; rinsed with water of pH 2.50; 3.50 and 4.50 and hot dip galvanized steel in 3.5% NaC1. Certain operational parameters were analyzed. such as the aging bath (HCl), and elimination of the rinsing stage, to observe their infiuence in the hot dip galvanizing coating. It was found that an increase of coating thickness of hot dip galvanizing steel decreased the corrosion rate and the microhardness. Surfaces of alloy layer of the coating were examined by scanning electron microscope (SEM). SEM measurements was determined that when obvious the nnsing, the chlorine can be catched between two layers (interface), and soon migrates of the outermost alloy layer of the coating (Delta) towards the imermost one (Garnma) |
| Disciplines: | Ingeniería |
| Keyword: | Ingeniería de materiales, Acero galvanizado, Inmersión caliente, Decapado, Zinc |
| Keyword: | Engineering, Materials engineering, Galvanized steel, Hot dip, Pickling, Zinc |
| Full text: | Texto completo (Ver HTML) |