| Journal: | Revista mexicana de ingeniería química |
| Database: | PERIÓDICA |
| System number: | 000403666 |
| ISSN: | 1665-2738 |
| Authors: | Tirado Guerra, S1 |
| Institutions: | 1Instituto Politécnico Nacional, Escuela Superior de Física y Matemáticas, México, Distrito Federal. México |
| Year: | 2015 |
| Season: | Sep-Dic |
| Volumen: | 14 |
| Number: | 3 |
| Pages: | 691-701 |
| Country: | México |
| Language: | Inglés |
| Document type: | Artículo |
| Approach: | Experimental, aplicado |
| Spanish abstract | Películas delgadas de SnO2 fueron crecidas sobre sustratos de vidrio sodo-cálcico empleando la técnica de sol-gel y el procedimiento de inmersión repetida. De cloruro de estaño se preparó una solución a 0.2 M en 2-metoxietanol y la monoetanolamina como estabilizador. La serie de películas preparadas SnO2 resultaron de un espesor de 150 nm aproximadamente. Una vez preparadas dichas películas se modificaron superficialmente depositando nanopartículas de plata, a partir de una solución a baja concentración de nitrato de plata en etanol, empleando la técnica de depósito mencionada anteriormente, obteniendo así la serie SnO2:Agn, con n= 0, 1, 3, 5 y 10, que indica el número de veces que fueron impregnadas con la solución de plata. Ambas series de películas se caracterizaron en su estructura por DRX, morfología por MEB y composición química por EDS, la forma y el tamaño de grano, así como la porosidad y rugosidad por MFA, sus propiedades eléctricas por cuatro y dos puntas, y las ópticas por UV-Vis. Para la serie de películas SnO2:Agn se determinaron sus propiedades como sensores del gas propano en el rango de concentración de 0-500 ppm y operando a temperaturas de 23, 100, 200 y 300 °C. Los resultados de una selección de sensores se presentan en este trabajo |
| English abstract | SnO2 thin films were fabricated by the sol-gel process and repeated immersion technique and deposited on soda-lime substrates. Tin chloride was used as precursor of tin, a 0.2 M solution in 2-methoxyethanol as a solvent and the monoethanolamine as a stabilizer was prepared. From silver nitrate a solution in ethanol was prepared and superficially incorporated onto SnO2 films, thus obtaining SnO2:Agn, where n= 0, 1, 3, 5 and 10 times impregnated with silver solution. A series of samples of approximately 150 nm thickness were prepared and were studied. Several layers of Ag were applied superficially on SnO2 films. The thin films thus obtained are characterized by their structure, XRD, morphology by SEM and chemical composition by EDS, grain shape and size, porosity and surface roughness by AFM, and their electrical and optical (UV-Vis). Properties of SnO2:Agn samples to propane gas detection in the range of 0-500 ppm gas concentration were tested operating at temperatures of 23, 100, 200 and 300 °C. The results of a selection of these sensors are presented in this paper |
| Disciplines: | Química |
| Keyword: | Ingeniería química, Sensores de gases, Películas delgadas, Dióxido de estaño, Sol-gel, Propano |
| Keyword: | Chemistry, Chemical engineering, Gas sensors, Thin films, Tin dioxide, Sol-gel, Propane |
| Full text: | Texto completo (Ver HTML) |