Revista: | Revista mexicana de física |
Base de datos: | PERIÓDICA |
Número de sistema: | 000425506 |
ISSN: | 0035-001X |
Autores: | Portillo Moreno, O1 Gutiérrez Pérez, R1 Chávez Portillo, M1 Márquez Specia, M.N1 Hernández Téllez, G1 Lazcano Hernández, M1 Moreno Rodríguez, A1 Palomino Merino, R2 Rubio Rosas, E3 |
Instituciones: | 1Benemérita Universidad Autónoma de Puebla, Facultad de Ciencias Químicas, Puebla. México 2Benemérita Universidad Autónoma de Puebla, Facultad de Ciencias Físico Matemáticas, Puebla. México 3Benemérita Universidad Autónoma de Puebla, Centro Universitario de Vinculación y Transferencia de Tecnología, Puebla. México |
Año: | 2016 |
Periodo: | Oct |
Volumen: | 62 |
Número: | 5 |
País: | México |
Idioma: | Inglés |
Tipo de documento: | Artículo |
Enfoque: | Analítico, teórico |
Resumen en inglés | Nanocrystalline PbS films grown by chemical bath at T = 40 ± 2 oC onto glass slides were modified by in situ Co2+ -doping and their structural and optical properties were examined. By FT-IR spectra, a sharp stretching mode can be seen at ~1384 cm-1 due to the vibration mode of C O 3 2 ions. XRD patterns shown the growth on the zinc blende crystalline face. The grain size was determined by using X-rays diffractograms and was found at ~28 nm and ~13 - 25 nm for undoped and doped samples, respectively. Optical absorption spectra was used for calculating the energy band gap, and displayed a shift in the ~1:21 - 2:21 eV range, associated with quantum confinement effect. Raman peaks at ~ 210, 271, and 451 cm-1, corresponding to a 1LO phonon mode, a two-phonon process, and a 2LO phonon mode respectively were also recorded. The surface and grain size of the films were measured by AFM studies |
Disciplinas: | Física y astronomía |
Palabras clave: | Física, Películas delgadas, Nanocristales, Cuántica, Efecto de confinamiento |
Keyword: | Dopaje, Physics, Thin films, Nanocrystals, Quantum, Confinement effect, Doping |
Texto completo: | Texto completo (Ver HTML) Texto completo (Ver PDF) |