| Journal: | Momento |
| Database: | PERIÓDICA |
| System number: | 000406896 |
| ISSN: | 0121-4470 |
| Authors: | Quiroz, Heiddy P1 Dussan, Anderson1 Quintero, Francisco2 Arias, Pedro J2 Zea, Hugo R2 |
| Institutions: | 1Universidad Nacional de Colombia, Departamento de Física, Bogotá. Colombia 2Universidad Nacional de Colombia, Facultad de Ingeniería, Bogotá. Colombia |
| Year: | 2014 |
| Season: | Dic |
| Number: | 49 |
| Pages: | 36-46 |
| Country: | Colombia |
| Language: | Español |
| Document type: | Artículo |
| Approach: | Analítico, descriptivo |
| Spanish abstract | En este trabajo se fabricaron arreglos de nanotubos de TiO2 por el método de anodizado electroquímico usando tanto para el ánodo como para el cátodo láminas de Ti y diferentes voltajes de anodización. Para la preparación de las muestras se usó una mezcla de agua y solución de etilenglicol a temperatura ambiente cambiando el tiempo de síntesis durante la reacción. Se realizaron procesos de recocido a todas las muestras en el rango entre 273 y 723 K, sin observarse cambios en las propiedades morfológicas del material. A partir de medidas de difracción de rayos X fueron identificadas las fases rutilo y anatasa en todas las muestras; cuando la temperatura de recocido superó los 723 K, se observó un cambio estructural de la fase anatasa a rutilo. A partir de medidas de SEM se observó que el tamaño del diámetro interno de los nanotubos varió entre 37 nm y 41 nm cuando el voltaje de anodización fue alternante y constante, respectivamente. Se observó que un tamaño de ~6 um de longitud y 29,56 nm de espesor de la barrera del tubo están influenciados por el voltaje de anodización constante de 80 V; sin embargo nanotubos con forma de guadua se evidenciaron cuando se aplicó un voltaje alternante de 80 V y 20 V durante 1 minuto y 5 minutos respectivamente. Se presenta una correlación entre los parámetros de síntesis y las propiedades morfológicas |
| English abstract | In this work TiO2 nanotubes arrays were obtained by electrochemical anodization method using Ti foil, both anode and cathode, and under different anodization voltages. A mix of water and ethylene glycol as electrolyte was used at environment temperature for several times of reaction. Annealing process to TiO_2 samples were realized at temperature between 273 and 723 K without changes on morphological properties. Rutile and anatase phases were identified by X-ray diffraction measurements in all samples and a change of anatase to rutile phase was observed at biggest annealing temperature (T=723 k). From SEM measurements the inner diameter size for nanotubes were obtained, varying between 37 nm and 41 nm when anodizing voltage was alternant and constant, respectively. Nanotubes with ~6 um of length and 29.56 nm thickness of barrier layer were obtained as influence of the anodizition voltage of 80 V fixed; however nanotubes with bamboo form were observed at alternant voltage of 80 and 20 V during 1 minute and 5 minutes, respectively. A correlation between deposition parameters and morphological properties is presented |
| Disciplines: | Física y astronomía, Ingeniería |
| Keyword: | Física de materia condensada, Ingeniería de materiales, Nanoestructuras, Dióxido de titanio, Nanotubos, Titanio, Voltaje |
| Keyword: | Physics and astronomy, Engineering, Condensed matter physics, Physics, Materials engineering, Nanostructures, Titanium dioxide, Nanotubes, Titanium, Voltage |