| Journal: | Biotecnología en el sector agropecuario y agroindustrial |
| Database: | PERIÓDICA |
| System number: | 000419375 |
| ISSN: | 1692-3561 |
| Authors: | Toro, Fernando1 Mina, José Herminsul2 Bolaños, Carlos Andrés3 |
| Institutions: | 1Universidad San Buenaventura, Programa de Ingeniería de Materiales, Cali, Valle del Cauca. Colombia 2Universidad del Valle, Escuela de Ingeniería de Materiales, Cali, Valle del Cauca. Colombia 3Universidad del Valle, Facultad de Ingeniería, Cali, Valle del Cauca. Colombia |
| Year: | 2013 |
| Season: | Ene-Jun |
| Volumen: | 11 |
| Number: | 1 |
| Pages: | 30-36 |
| Country: | Colombia |
| Language: | Español |
| Document type: | Artículo |
| Approach: | Analítico, descriptivo |
| Spanish abstract | En este trabajo se estudiaron las propiedades físico-químicas, térmicas y mecánicas de la resina Mopa-Mopa (MM), también conocida como barniz de pasto, extraída de la yema de la planta Elaeagia pastoensis Mora. El proceso de extracción del material se llevó a cabo mediante de una lixiviación en caliente, empleando etanol como disolvente. A partir de la resina MM previamente obtenida, se elaboraron los especímenes de ensayo siguiendo un proceso de moldeo por compresión en caliente con ayuda de una prensa de platos calefactores. Las muestras se secaron a 80°C por 24 horas y posteriormente se acondicionaron a tres humedades relativas (H.R.) diferentes (47 ± 2%, 77± 2%, y 97 ± 2%). El análisis termogravimétrico (TGA), en la resina MM reveló que el material presentó estabilidad térmica hasta aproximadamente 230°C, sugiriendo esto que es factible llegar a transformarlo por la vía térmica. Por otro lado, con la prueba de Calorimetría Diferencial de Barrido (DSC) se estableció que la resina MM presentó algún grado de semicristalinidad. Finalmente, la absorción de humedad y las propiedades mecánicas exhibidas fueron una función directa de las diferentes H.R. empleadas en el acondicionamiento |
| English abstract | In this paper we studied the physico-chemical, thermal and mechanical properties of the Mopa Mopa (MM) resin, also known as varnish Pasto, obtained it from the leaf bud of the elaegia pastoensis Mora tree. The extraction process of the material is carried out by a hot leach, using ethanol as solvent. Using the MM resin the previously obtained, were prepared test specimens using a process of hot compression molding using a heating plate press. The samples were dried at 80°C for 24 hours and then conditioned at three different relative humidities (R.H.) (47 ± 2%, 77 ± 2% and 97 ± 2%). Thermogravimetric analysis (TGA) in the MM resin revealed that the material showed thermal stability up to about 230°C, indicating that it is feasible to transform it by a thermal process. Later, tests Differential Scanning Calorimetry (DSC) was established that the MM resin had some degree of semi-crystallinity. Finally, moisture absorption and the mechanical properties presented were directly proportional to the different R.H. used on the preparation |
| Portuguese abstract | Neste trabalho foram estudadas as propriedades físico-químicas, térmicas e mecânicas da resina Mopa-Mopa (MM), também conhecido como verniz do Pasto, extraídas da gema planta elaeagia pastoensis Mora. O processo de extração do material é realizado utilizando uma lixiviação quente, usando etanol como solvente. A partir da resina MM obtido anteriormente, foram preparados os espécimes de ensaio, utilizando um processo de moldagem por compressão a quente usando uma prensa de pratos de aquecimento. As amostras foram secas a 80°C durante 24 horas e depois condicionada menos três diferentes humidades relativas (H.R.) (47 ± 2%, 77 ± 2% e 97 ± 2%). A análise termogravimétrica (TGA) na resina MM revelou que o material mostrou estabilidade térmica até cerca de 230°C, indicando que é viável para transformar a via térmica. Além disso, a evidência de calorimetria diferencial exploratória (DSC) foi estabelecido que o resina MM apresentaram algum grau de semicristalinidad. Finalmente, a absorção de umidade e as propriedades mecânicas apresentadas foram uma função direta do diferente H.R. utilizado na preparação |
| Disciplines: | Biología |
| Keyword: | Angiospermas, Resinas vegetales, Elaeagia pastoensis, Humedad relativa, Propiedades fisicomecánicas, Propiedades térmicas |
| Keyword: | Angiosperms, Plant resins, Elaeagia pastoensis, Relative humidity, Physicomechanical properties, Thermal properties |
| Full text: | Texto completo (Ver HTML) |