| Revista: | Tecnologia em metalurgia e materiais |
| Base de datos: | PERIÓDICA |
| Número de sistema: | 000333133 |
| ISSN: | 1807-300X |
| Autores: | Medeiros, Neil de1 Moreira, Luciano Pessanha1 Lins, Jefferson Fabricio Cardoso1 Gouvea, Jayme Pereira de1 Silva, Fabiane Roberta Freitas da1 |
| Instituciones: | 1Universidade Federal Fluminense, Programa de Pos-graduacao em Engenharia Metalurgica, Volta Redonda, Rio de Janeiro. Brasil |
| Año: | 2009 |
| Periodo: | Abr-Jun |
| Volumen: | 5 |
| Número: | 4 |
| Paginación: | 193-197 |
| País: | Brasil |
| Idioma: | Portugués |
| Tipo de documento: | Artículo |
| Enfoque: | Experimental, aplicado |
| Resumen en inglés | An IF steel billet was deformed via equal channel angular pressing (ECAP) using a single pass at room temperature. Grain refinement was observed in the microstructure after severe plastic deformation. Regular deformation bands arise in several grains as a result of grain fragmentation during the pressing. The hardness profile shows an extended homogeneity region within the deformed area due to the tooling (bend radius) employed |
| Resumen en portugués | Um tarugo de aço IF foi deformado pela técnica de prensagem por canais equiangulares (Equal Channel Angular Pressing – ECAP) num único passe a temperatura ambiente. A partir da observação da sua microestrutura pode-se comprovar que houve um intenso refinamento dos grãos. Também foi observado que na sua microestrutura surgiram bandas de deformação regulares em função de processos de subdivisão dos grãos. O perfil de dureza na área deformada mostrou a existência de uma região de homogeneidade extensa em função da configuração do ferramental (raio de adoçamento) utilizado |
| Disciplinas: | Ingeniería |
| Palabras clave: | Ingeniería metalúrgica, Acero inoxidable, Deformación plástica, Prensado |
| Keyword: | Engineering, Metallurgical engineering, Stainless steel, Plastic deformation, Pressing |
| Texto completo: | Texto completo (Ver PDF) |