Revista: | Tecnologia em metalurgia e materiais |
Base de datos: | PERIÓDICA |
Número de sistema: | 000333133 |
ISSN: | 1807-300X |
Autors: | Medeiros, Neil de1 Moreira, Luciano Pessanha1 Lins, Jefferson Fabricio Cardoso1 Gouvea, Jayme Pereira de1 Silva, Fabiane Roberta Freitas da1 |
Institucions: | 1Universidade Federal Fluminense, Programa de Pos-graduacao em Engenharia Metalurgica, Volta Redonda, Rio de Janeiro. Brasil |
Any: | 2009 |
Període: | Abr-Jun |
Volum: | 5 |
Número: | 4 |
Paginació: | 193-197 |
País: | Brasil |
Idioma: | Portugués |
Tipo de documento: | Artículo |
Enfoque: | Experimental, aplicado |
Resumen en inglés | An IF steel billet was deformed via equal channel angular pressing (ECAP) using a single pass at room temperature. Grain refinement was observed in the microstructure after severe plastic deformation. Regular deformation bands arise in several grains as a result of grain fragmentation during the pressing. The hardness profile shows an extended homogeneity region within the deformed area due to the tooling (bend radius) employed |
Resumen en portugués | Um tarugo de aço IF foi deformado pela técnica de prensagem por canais equiangulares (Equal Channel Angular Pressing – ECAP) num único passe a temperatura ambiente. A partir da observação da sua microestrutura pode-se comprovar que houve um intenso refinamento dos grãos. Também foi observado que na sua microestrutura surgiram bandas de deformação regulares em função de processos de subdivisão dos grãos. O perfil de dureza na área deformada mostrou a existência de uma região de homogeneidade extensa em função da configuração do ferramental (raio de adoçamento) utilizado |
Disciplines | Ingeniería |
Paraules clau: | Ingeniería metalúrgica, Acero inoxidable, Deformación plástica, Prensado |
Keyword: | Engineering, Metallurgical engineering, Stainless steel, Plastic deformation, Pressing |
Text complet: | Texto completo (Ver PDF) |