Revista: | Semina. Ciencias exatas e tecnologicas |
Base de datos: | PERIÓDICA |
Número de sistema: | 000367751 |
ISSN: | 1676-5451 |
Autores: | Gardes, Bernard J.L1 Alfaya, Antonio A.S1 Alfaya, Reni V.S1 Urbano, Alexander2 Scarminio, Jair2 |
Instituciones: | 1Universidade Estadual de Londrina, Departamento de Quimica, Londrina, Parana. Brasil 2Universidade Estadual de Londrina, Departamento de Fisica, Londrina, Parana. Brasil |
Año: | 2009 |
Periodo: | Jul-Dic |
Volumen: | 30 |
Número: | 2 |
Paginación: | 91-98 |
País: | Brasil |
Idioma: | Portugués |
Tipo de documento: | Artículo |
Enfoque: | Experimental, aplicado |
Resumen en inglés | LiMn2O4 and LiCr0.2Mn1.8O4 powders were synthesized by Pechini process, modified in order to reduce the number of steps and to work at temperatures below or equal to 400oC. Both phases crystallize in the same spinel structure with lattice constants of 8.21 and 8.22 Å respectively. Although the annealing temperature was low, the cristallinity is good and no residual amounts of organic material were detected |
Resumen en portugués | As fases LiMn2O4 e LiCr0,2Mn1,8O4 em pó foram preparadas por processo Pechini, modificado de maneira a diminuir o número de etapas e trabalhar com temperaturas inferiores ou iguais a 400oC. As 2 fases cristalizam no mesmo arranjo espinélio, com parâmetros de rede iguais a 8,21 e 8,22 Å respectivamente. Embora com temperatura de recozimento baixa, elas apresentaram boa qualidade cristalina e ausência de contaminação por resíduos orgânicos |
Disciplinas: | Química |
Palabras clave: | Electroquímica, Oxidos litiados, Síntesis química, Proceso de Pechini, Cristalización |
Keyword: | Chemistry, Electrochemistry, Lithium oxide, Chemical synthesis, Pechini process, Crystallization |
Texto completo: | Texto completo (Ver HTML) |