| Revista: | Revista Colombiana de Química |
| Base de datos: | PERIÓDICA |
| Número de sistema: | 000435162 |
| ISSN: | 0120-2804 |
| Autores: | Sosa, Alexis Alberto1 Romanelli, Gustavo Pablo1 Pizzio, Luis René1 |
| Instituciones: | 1Universidad Nacional de La Plata, Facultad de Ciencias Exactas, La Plata, Buenos Aires. Argentina |
| Año: | 2020 |
| Periodo: | May-Ago |
| Volumen: | 49 |
| Número: | 2 |
| País: | Colombia |
| Idioma: | Español |
| Tipo de documento: | Artículo |
| Enfoque: | Experimental, analítico |
| Resumen en español | Se sintetizaron catalizadores (SNX#WPA) basados en ácido tungstofosfórico, en soportes de nanoestructuras de sílice (SNX), con distribución de diámetros y tamaños de mesoporos variables. Las SNX se prepararon en medio de octano/agua, usando poliestireno y bromuro de cetiltrimetilamonio como plantillas. Los materiales se caracterizaron por DRX, TEM y adsorción/desorción de nitrógeno. La relación octano/agua influyó tanto en la morfología y el tamaño de las SNX como en la distribución del tamaño de poro. Las SNX obtenidas utilizando relaciones OCT/H2O en el rango de 0,07-0,35, presentan mesoporos pequeños (5-6 nm) y grandes (28-34 nm), generados principalmente por poliestireno. Los mesoporos grandes y su contribución de volumen fueron claramente más altos que en las muestras SN1, SN2 y SN3. La estructura y la morfología de SNX#WPA fueron similares a las de las SNX usadas como soporte. Además, la caracterización de todos los materiales SNX#WPA por FT-IR y 31P NMR indicó la presencia de especies [PW12O40]3- y [H3-XPW12O40](3-X)- sin degradar. Según los resultados de la valoración potenciométrica, los sólidos presentaron sitios ácidos muy fuertes. Se evaluó la actividad de SNX#WPA como catalizadores en la síntesis de quinoxalinas, a partir de lo cual se obtuvieron altos rendimientos, sin formación de subproductos. De ello resultó que los materiales preparados son catalizadores altamente selectivos y reutilizables |
| Resumen en inglés | Tungstophosphoric acid supported on silica nanostructures (SNX#WPA) with variable diameter and mesopore size distribution were synthetized. Silica nanostructures (SNX) were prepared in octane/aqueous media using polystyrene and CTAB as organic templates. The materials were characterized by XRD, SEM, TEM and dinitrogen adsorption/ desorption isotherm analysis. The octane/ water ratio influenced the morphology and size of SNX prepared, as well as its pore size distribution. The SNX samples obtained using OCT/H2O ratios in the range 0.07-0.35 (SN4, SN5, and SN6 samples). present small (5-6 nm) and large (28-34 nm) mesopores (mainly generated by polystyrene). Large mesopores and their volume contribution were clearly higher than in the SN1, SN2, and SN3 samples. The structure and morphology of SNX#WPA samples were similar to those of the SNX. Furthermore, the characterization of all the SNX#WPA materials by FT-IR and 31P NMR indicated the presence of undegraded [PW12O40]3- and [H3-XPW12O40](3-X)-species. According to the potentiometric titration results, the solids presented very strong acid sites. The performance of SNX#WPA materials as catalysts in the synthesis of quinoxalines was evaluated. The yields achieved were high, without formation of by-products resulting from competitive reactions or decomposition products, so the prepared materials are highly selective and reusable catalysts |
| Resumen en portugués | Catalisadores (SNX#WPA) baseados em ácido tungsofosfórico suportado em nanoestruturas de sílica (SNX) foram sintetizados com distribuição de tamanhos e diâmetros variados de mesoporos. Os SNX foram preparados em meio octano/aquoso usando poliestireno e brometo de cetiltrimetilamônio como modelos orgânicos. Os materiais foram caracterizados por DRX, TEM e adsorção/ dessorção de nitrogénio. A razão octano/ agua influenciou a morfologia e o tamanho do SNX, bem como a distribuição do tamanho dos poros. O SNX obtido usando razões OCT/ H2O na faixa de 0,07-0,35, possui mesoporos pequenos (5-6 nm) e grandes (28-34 nm) (gerados principalmente por poliestireno). Mesoporos grandes e sua contribuição em volume foram claramente maiores do que nas amostras SN1, SN2 e SN3. A estrutura e a morfologia do SNX#WPA foram semelhantes às do SNX usado como suporte. Além disso, a caracterização de todos os materiais SNX#WPA por FT-IR e 31P NMR indicou a presença das espécies [PW12O40]3- e [H3-XPW12O40](3-X)- sem degradar. De acordo com os resultados da titulação potenciométrica, os sólidos apresentaram locais ácidos muito fortes. A atividade do SNX#WPA como catalisadores na síntese de quinoxalinas foi avaliada, produzindo altos rendimentos, sem formação de subprodutos, resultando em materiais catalisadores altamente seletivos e reutilizáveis |
| Disciplinas: | Química |
| Palabras clave: | Fisicoquímica y química teórica, Sílice, Nanoestructuras, Acido tungstofosfórico, Catálisis, Heteropoliácidos, Heterociclos, Quinoxalina |
| Keyword: | Physical and theoretical chemistry, Silica, Nanostructures, Catalysis, Heteropolyacids, Heterocycles, Quinoxaline |
| Texto completo: | Texto completo (Ver HTML) Texto completo (Ver PDF) |