| Revista: | Revista ADM |
| Base de datos: | PERIÓDICA |
| Número de sistema: | 000377908 |
| ISSN: | 0001-0944 |
| Autores: | Rivera Guajardo, Renel Victoria Méndez Maya, Roberto1 Escalante Balderas, Silvia Alicia1 Cornejo Peña, María Antonieta1 Nishimura Imai, Alberto Tadashi1 Oliver Parra, Rogelio1 |
| Instituciones: | 1Universidad Autónoma de Tamaulipas, Facultad de Odontología, Tampico, Tamaulipas. México |
| Año: | 2014 |
| Periodo: | May-Jun |
| Volumen: | 71 |
| Número: | 3 |
| Paginación: | 142-146 |
| País: | México |
| Idioma: | Español |
| Tipo de documento: | Artículo |
| Enfoque: | Experimental |
| Resumen en español | El acabado y pulido convencional de bases para dentadura debe reducir la rugosidad superficial residual para lograr una superfi cie lisa, tersa y brillante con el objetivo de disminuir la adhesión bacteriana. Objetivo: Comparar la rugosidad superfi cial de tres resinas acrílicas para una base de dentadura: ProBase-Hot (PH), NicTone (NT) y Lucitone 199 (LT) al ser tratadas con el sistema de acabado y pulido convencional. Material y métodos: Una muestra de 27 especímenes de diferentes resinas para base de dentadura; PH, NT y LT (n = 9), se sometieron al acabado y pulido bajo los siguientes tratamientos: cara A, acabado con fresa de carburo de tungsteno, y cara B, acabado y pulido convencional; posteriormente se registró la rugosidad con perfi lómetro y se obtuvieron imágenes bajo microscopio electrónico de barrido (MEB) a 35X registrando la rugosidad superficial basal y post-tratamiento en ambas caras. Los datos se analizaron con prueba t pareada e independiente (α 0.05) en el programa SPSS 18.0. Resultados: La rugosidad postratamiento con LT fue 0.183 μm, para PH 0.217 μm y NT 0.329 μm; (p = 0.001). Los grupos LT y PH mostraron una reducción signifi cativa de la rugosidad después de pulirlas con el sistema convencional y un aspecto superfi cial más uniforme bajo observación al MEB. Conclusiones: El acabado y pulido convencional de LT propicia una baja rugosidad dejando menos del 25% de huecos y poros en su superficie. El grupo NT presenta una superfi cie con mayor cantidad de huecos, ranuras y ralladuras |
| Resumen en inglés | Conventional finishing and polishing of denture bases should reduce residual surface roughness to achieve a smooth, soft, shiny surface and so reduce bacterial adhesion. Objective: To compare the effect on the surface roughness of three acrylic resin denture base materials—ProBase-Hot (PH), NicTone (NT), and Lucitone 199 (LT)—of conventional polishing and fi nishing. Material and Methods: A sample of 27 resin denture base materials, PH, NT, and LT (n = 9), were subjected to fi nishing and polishing as follows: side A fi nished using a tungsten carbide drill, and side B using conventional fi nishing and polishing. Surface roughness was subsequently measured using a profi lometer and images obtained using a Scanning Electron Microscope (SEM) at a magnifi cation of 35X. Baseline and post-treatment surface roughness were recorded for both sides. Using SPSS 18.0 statistics software, data were analyzed by means of the paired t-test and independent t-test (α 0.05). Results: For LT, the post-treatment roughness was 0.183 μm; for PH it was 0.217 μm, and for NT, 0.329 μm (p = 0.001). The LT and PH groups showed a signifi cant reduction in roughness after polishing using the conventional system and a more uniform surface appearance under SEM observation. Conclusions: In the case of LT, conventional fi nishing and polishing results in a low level of roughness with over 25% of the pits and pores on its surface removed. In the case of NT, the surface displayed a greater number of pits, grooves, and scratches |
| Disciplinas: | Medicina |
| Palabras clave: | Odontología, Terapéutica y rehabilitación, Dentadura, Resinas, Rugosidad superficial, Porosidad, Pulido |
| Keyword: | Medicine, Dentistry, Therapeutics and rehabilitation, Denture, Resins, Surface roughness, Porosity, Polish |
| Texto completo: | Texto completo (Ver PDF) |