| Revista: | REM. Revista Escola de Minas |
| Base de datos: | PERIÓDICA |
| Número de sistema: | 000313844 |
| ISSN: | 0370-4467 |
| Autores: | Pereira, Renato Alves1 Mendes-Filho, Antonio Alves2 Araujo, Fernando Gabriel da Silva |
| Instituciones: | 1Universidade Federal de Ouro Preto, Ouro Preto, Minas Gerais. Brasil 2Centro Paula Souza, Sao Paulo. Brasil |
| Año: | 2006 |
| Periodo: | Abr-Jun |
| Volumen: | 59 |
| Número: | 2 |
| Paginación: | 207-212 |
| País: | Brasil |
| Idioma: | Portugués |
| Tipo de documento: | Artículo |
| Enfoque: | Analítico, descriptivo |
| Resumen en inglés | Barium titanate powders were produced by hydrothermal synthesis, at 220ºC, for 20 hours, in stoichiometric composition and doped with lantanum varying from 0.2 to 1.0mol%.The powders were characterized by x-ray diffraction and then pressed at 3,000 kgf to form discs. The discs were sinterized on air at 1250ºC for 5 hours and characterized by x-ray diffraction, scanning electron microscopy and complex impedanciometry |
| Resumen en portugués | Pós de titanato de bário foram produzidos por síntese hidrotérmica, a 220°C, por 20h, na forma estequiométrica pura e dopada com concentrações de lantânio entre 0,2 e 1,0mol%. Os pós foram caracterizados por difração de raios X e, em seguida, prensados a 3000kgf, na forma de pastilhas. As pastilhas foram sinterizadas ao ar a 1250ºC por 5h e caracterizadas por difração de raios X, microscopia eletrônica de varredura e impedanciometria complexa |
| Disciplinas: | Ingeniería |
| Palabras clave: | Ingeniería metalúrgica, Síntesis hidrotérmica, Dopaje, Sinterización |
| Keyword: | Engineering, Metallurgical engineering, Hydrothermal synthesis, Doping, Sintering |
| Texto completo: | Texto completo (Ver HTML) |