| Revista: | Quimica nova |
| Base de datos: | PERIÓDICA |
| Número de sistema: | 000198156 |
| ISSN: | 0100-4042 |
| Autores: | Ribeiro, Roberto Ananias1 Mohallem, Nelcy Della Santina https://biblat.unam.mx/pt/frecuencias/autor1 |
| Instituciones: | 1Universidade Federal de Minas Gerais, Departamento de Quimica, Belo Horizonte, Minas Gerais. Brasil |
| Año: | 2001 |
| Periodo: | Nov-Dic |
| Volumen: | 24 |
| Número: | 6 |
| Paginación: | 773-777 |
| País: | Brasil |
| Idioma: | Portugués |
| Tipo de documento: | Artículo |
| Enfoque: | Experimental |
| Resumen en inglés | The preparation of g-LiAlO2 by coprecipitation and sol-gel synthesis was investigated. Ceramic powders obtained by coprecipitation synthesis were prepared from aqueous solutions of aluminum and lithium nitrates using sodium hydroxide as precipitant agent. By sol-gel synthesis, the ceramic powders were prepared from hydrolysis of aluminum isopropoxide. The materials obtained by two routes of synthesis were dried at 80oC and calcined at 550, 750, 950 and 1150oC. The characterization was done by X-ray diffraction, infrared spectroscopy, emission and absorption atomic spectrometry, helium picnometry, specific surface area (BET method) and scanning electronic microscopy. Mixtures of crystalline phases were obtained by coprecipitation synthesis: 80oC- LiAl2(OH)7.2H2O + Al(OH)3; 550 and 750oC- a-LiAlO2 + h-Al2O3; 950 and 1150oC- g-LiAlO2 + LiAl5O8. Chemical analysis showed molar ration Al/Li @ 3. Crystalline single-phases were obtained by sol-gel synthesis above 550oC: 550oC-a-LiAlO2; 750, 950 and 1150oC-g-LiAlO2. These powders presented molar ration Al/Li @ 1. Thus, g-LiAlO2 crystalline phase was obtained at 750oC by sol-gel synthesis while by coprecipitation synthesis, a mixture of crystalline phases was obtained. These results showed the superiority of the sol-gel synthesis for the preparation of pure g-LiAlO2 |
| Disciplinas: | Ingeniería, Química |
| Palabras clave: | Ingeniería de materiales, Química analítica, Química inorgánica, Aluminatos, Litio, Cerámica, Polvos cerámicos, Coprecipitación, Síntesis sol-gel, Caracterización |
| Keyword: | Engineering, Chemistry, Materials engineering, Analytical chemistry, Inorganic chemistry, Aluminates, Lithium, Ceramics, Ceramic powders, Coprecipitation, Sol-gel synthesis, Characterization |
| Texto completo: | Texto completo (Ver HTML) |