Pechini synthesis and microstructure of nickel-doped copper chromites
Título del documento: Pechini synthesis and microstructure of nickel-doped copper chromites
Revista: Materials research
Base de datos: PERIÓDICA
Número de sistema: 000312832
ISSN: 1516-1439
Autores: 1
Instituciones: 1Universidade Federal do Rio Grande do Norte, Departamento de Quimica, Natal, Rio Grande do Norte. Brasil
Año:
Periodo: Abr-Jun
Volumen: 8
Número: 2
Paginación: 221-224
País: Brasil
Idioma: Inglés
Tipo de documento: Nota breve o noticia
Enfoque: Experimental
Resumen en inglés Spinel-type solid solutions were synthesized by the Pechini method and calcined between 500 and 900 °C for 4 hours and at 900 °C for 8 hours to produce ceramic pigments. The resulting powders were characterized by thermogravimetric analysis, Fourier-transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), scanning electron microscopy (SEM), particle size analysis and BET surface area measurements. The formation of spinel took place upon calcination at 700 °C. IR spectroscopy revealed the presence of n1 and n2 bands, typical of spinel structures, broadened by the presence of more than one cationic species in the structure. The specific area of the resulting powder decreased from 24.7 to 1.4 m² g-1 as the calcination temperature increased from 700 to 900 °C. Microstructural analyses revealed the presence of crystalline spinel as the only phase present in powders calcined at 900 °C. Colorimetric analyses using L*a*b* coordinates and UV-visible spectroscopy revealed that the pigment was predominantly black
Disciplinas: Ingeniería,
Química
Palabras clave: Ingeniería de materiales,
Química industrial,
Espinelas,
Cerámica,
Síntesis química,
Cristalización,
Microestructuras,
Propiedades mecánicas
Keyword: Engineering,
Chemistry,
Materials engineering,
Industrial chemistry,
Spinels,
Ceramics,
Chemical synthesis,
Crystallization,
Microstructures,
Mechanical properties
Texto completo: Texto completo (Ver HTML)