| Revista: | Ecletica quimica |
| Base de datos: | PERIÓDICA |
| Número de sistema: | 000366674 |
| ISSN: | 0100-4670 |
| Autores: | Silva, R.A.G1 Magdalena, A.G1 Carvalho, T. M1 |
| Instituciones: | 1Universidade Estadual Paulista "Julio de Mesquita Filho", Instituto de Quimica, Araraquara, Sao Paulo. Brasil |
| Año: | 2008 |
| Periodo: | Ene-Mar |
| Volumen: | 33 |
| Número: | 1 |
| Paginación: | 63-70 |
| País: | Brasil |
| Idioma: | Portugués |
| Tipo de documento: | Artículo |
| Enfoque: | Experimental, aplicado |
| Resumen en inglés | Ag precipitation reaction in the Cu-8wt.%Al-6wt.%Ag alloys was studied using microhardness measurements with temperature and ageing time, X-ray diffraction patterns (DRX), differential scanning calorimetry (DSC) and scanning electron microscopy (SEM). The results obtained showed that the mechanism of Ag precipitation reaction is an Ag diffusion controlled process and reaction rate reaches a maximum at about 500ºC |
| Resumen en portugués | A reação de precipitação de prata na liga Cu-8%Al-6%Ag foi estudada usando medidas de variação da microdureza com a temperatura e o tempo de envelhecimento, difratometria de raios X (DRX), calorimetria exploratória diferencial (DSC), microscopia eletrônica de varredura (MEV). Os resultados obtidos indicaram que o mecanismo da reação de precipitação da prata é um processo controlado pela difusão da prata e a velocidade desta reação atinge um máximo em torno de 500°C |
| Disciplinas: | Química |
| Palabras clave: | Química metalúrgica, Aleaciones, Cobre, Plata, Microdureza |
| Keyword: | Chemistry, Metallurgical chemistry, Alloys, Copper, Silver, Microhardness |
| Texto completo: | Texto completo (Ver HTML) |