| Revista: | Avances en química |
| Base de datos: | PERIÓDICA |
| Número de sistema: | 000352793 |
| ISSN: | 1856-5301 |
| Autores: | Rojas, Luis1 Halah, Amal El1 Contreras, Jesús1 Romero, Milagros1 Rangel, Elizabeth1 López Carrasquero, Francisco1 |
| Instituciones: | 1Universidad de Los Andes, Facultad de Ciencias, Mérida. Venezuela |
| Año: | 2011 |
| Volumen: | 6 |
| Número: | 2 |
| Paginación: | 21-28 |
| País: | Venezuela |
| Idioma: | Español |
| Tipo de documento: | Artículo |
| Enfoque: | Experimental |
| Resumen en español | En el presente trabajo se describe la copolimerización de la acrilamida (AAm) con el itaconato de monometoxietilo (IME) y el itaconato de dimetoxietilo (IDE) en varias proporciones molares. Las polimerizaciones se llevaron a cabo tanto en masa como en solución utilizando como iniciadores 2,2´- azobisisobutironitrilo (AIBN) y persulfato de amonio, respectivamente. Los copolímeros obtenidos resultaron ser solubles en agua y los mismos fueron analizados mediante espectroscopia FTIR y análisis termogravimétrico (TGA y DTGA). Los copolímeros AAm/IDE se obtuvieron con altos rendimientos y resultaron térmicamente estables hasta los 200°C, mientras que los rendimientos de los AAm/IME, fueron menores y comienzan a perder peso a los 150°C. Finalmente, se prepararon Hidrogeles AAm/IME y AAm/IDE empleando una proporción 80/20 molar y un 1% de entrecruzante. Se estudió la capacidad de hinchamiento de estos materiales encontrándose que en ambos casos ésta es superior a la del hidrogel de AAm pura preparado en las mismas condiciones |
| Resumen en inglés | The copolymerization of acrylamide (AAm) with monomethoxyethyl itaconate (IME) and dimethoxyethyl itaconate (IDE) was studied, using various molar relations AAm/itaconate. The polymerization reactions were carried out both in bulk and in solution, using 2,2´- azobisisobutyronitrile and ammonium persulfate respectively as initiators. The copolymers obtained were soluble in water and these were characterized by means FTIR spectroscopy and Thermogravimetric analysis (TGA and DTGA). The copolymers AAm/IDE were obtained with high yields and they were thermally stable up to 200ºC, whereas the yields of the copolymers AAm/IME were lower and they were stable up to 150ºC. Finally, hydrogels AAm/IME and AAm/IDE were prepared using the molar relation AAm/Itaconate 80/20 with 1% of crosslinking agent. It was found that swelling of these hydrogels was higher than those obtained with AAm in the same experimental conditions |
| Disciplinas: | Química |
| Palabras clave: | Fisicoquímica y química teórica, Química de polímeros, Química orgánica, Acrilamida, Itaconato de monometoxietilo, Itaconato de dimetoxietilo, Copolimerización |
| Keyword: | Chemistry, Organic chemistry, Physical and theoretical chemistry, Polymer chemistry, Acrylamide, Monomethoxyethyl itaconate, Dimethoxyethyl itaconate, Copolymerization |
| Texto completo: | Texto completo (Ver PDF) |