| Revista: | Revista técnica de la Facultad de Ingeniería. Universidad del Zulia |
| Base de datos: | PERIÓDICA |
| Número de sistema: | 000414275 |
| ISSN: | 0254-0770 |
| Autores: | Molina. Alessandra1 Rubio, Elisbeth1 Rodríguez, Douglas1 Solano, Roger1 Liotta, Leonarda2 Ferrer, Víctor1 |
| Instituciones: | 1Universidad del Zulia, Instituto de Superficies y Catálisis, Maracaibo, Zulia. Venezuela 2Istituto per lo Studio dei Materiali Nanostrutturati, Palermo, Sicilia. Italia |
| Año: | 2017 |
| Periodo: | Dic |
| Volumen: | 40 |
| Número: | 3 |
| Paginación: | 185-193 |
| País: | Venezuela |
| Idioma: | Español |
| Tipo de documento: | Artículo |
| Enfoque: | Aplicado, descriptivo |
| Resumen en español | Se prepararon catalizadores de Pd soportados sobre Al2 O3 , CeO2 /La2 O3 -Al2 O3 , Ce0,73Tb0,27Oδ-x/La2 O3 -Al2 O3 y Ce0,6Zr0,4Ox / La2 O3 -Al2 O3 , utilizando la técnica de impregnación a humedad incipiente. Los catalizadores fueron caracterizados mediante las técnicas de Fluorescencia de Rayos X (FRX), Difracción de Rayos X (DRX), Reducción a Temperatura Programada (RTP), Quimisorción de CO y Capacidad de Almacenamiento de Oxígeno (CAO). La actividad catalítica se estudió mediante la reacción de reducción de NO por CO en condiciones de alimentación estequiométricas. Los patrones de DRX mostraron que la cristalinidad de las muestras no es afectada por los tratamientos térmicos. Los resultados de RTP indicaron que la adición de Tb o Zr promovió la reducibilidad del óxido de cerio a más baja temperatura y la formación de la fase β-PdHx después de dos ciclos de reacción, así como un incremento en la CAO. La actividad catalítica mejoró luego de dos ciclos de reacción, siendo el catalizador más activo el de 0,5%Pd/Ce0,6Zr0,4Ox /La2 O3 -Al2 O3 . Este resultado sugiere cambios en la especies de PdO que junto con el óxido mixto CeZr, generan especies de mayor actividad |
| Resumen en inglés | Pd catalysts supported on Al2 O3 , CeO2 /La2 O3 -Al2 O3 , Ce0,73Tb0,27Oδ-x/La2 O3 -Al2 O3 and Ce0,6Zr0,4Ox /La2 O3 -Al2 O3 were prepared, using the incipient wetness impregnation technique. The catalysts were characterized by the techniques of X-ray Fluorescence (XRF), X-ray Diffraction (XRD), Temperature Programmed Reduction (TPR), CO Chemisorption and Oxygen Storage Capacity (OSC). The catalytic activity was studied by the reaction of reduction of NO by CO in stoichiometric feed conditions. XRD patterns showed that the crystallinity of the samples was not affected by thermal treatments. TPR results showed that addition of Tb or Zr promoted the reducibility of cerium oxide at lower temperature and the formation of β-PdHx phase after two reaction cycles as well as an increase in the OSC values. The catalytic activity after two reaction cycles was improved, being 0,5%Pd/Ce0,6Zr0,4Ox /La2 O3 -Al2 O3 the most active catalyst. This result suggests changes in PdO species that together with the CeZr mixed oxide, generated species that are more active |
| Disciplinas: | Ingeniería, Química |
| Palabras clave: | Ingeniería ambiental, Ingeniería química, Contaminación del aire, Catalizadores de paladio, Quimiosorción, Monóxido de carbono, Oxido de nitrógeno, Reducción a temperatura programada |
| Keyword: | Engineering, Chemistry, Chemical engineering, Environmental engineering, Air pollution, Palladium catalysts, Chemisorption, Carbon monoxide, Nitrogen oxide, Temperature programmed reduction |
| Texto completo: | Texto completo (Ver HTML) |