| Revista: | Revista técnica de la Facultad de Ingeniería. Universidad del Zulia |
| Base de datos: | PERIÓDICA |
| Número de sistema: | 000369210 |
| ISSN: | 0254-0770 |
| Autores: | Turris, Antonio de1 Romero, Matilde de1 Papavinasam, Sankara2 |
| Instituciones: | 1Universidad del Zulia, Facultad de Ingeniería, Maracaibo, Zulia. Venezuela 2CANMET, Materials Technology Laboratory, Hamilton, Ontario. Canadá |
| Año: | 2013 |
| Periodo: | Ago |
| Volumen: | 36 |
| Número: | 2 |
| Paginación: | 95-103 |
| País: | Venezuela |
| Idioma: | Español |
| Tipo de documento: | Artículo |
| Enfoque: | Aplicado, descriptivo |
| Resumen en español | Bajo ciertas condiciones, los hidrocarburos pueden alterar las condiciones de corrosión interna de los oleoductos y gasoductos. En este trabajo, se analizó el efecto de un crudo por la norma ASTM G205. Se analizó el punto de inversión de la emulsión, la humectabilidad de la superficie del acero y el efecto del crudo en la corrosión general y localizada de acero al carbono en agua de producción sintética con bacterias reductoras de sulfato (BSR) y dióxido de carbono (CO2). El punto de inversión se determinó midiendo la resistencia de la emulsión agua/crudo, y la humectabilidad se determinó midiendo la resistencia por el método de dispersión. Las pruebas de corrosividad de la fase acuosa se realizaron en una caja rotatoria. Durante las pruebas se midió el pH, se contabilizaron las BSR planctónicas, y las concentraciones de iones de sulfuro, sulfato, hierro, calcio y magnesio en la solución. Después de los experimentos, se contabilizaron las BSR sésiles |
| Resumen en inglés | Under certain conditions, hydrocarbons may alter the internal corrosion conditions of oil and gas pipelines. In this paper, the effects of a crude oil have been analyzed using the ASTM G205 Standard Guide. The emulsion inversion point (EIP), the wettability of the steel surface and the effect of crude oil on the general and localized corrosion of carbon steel in synthetic produced water with sulfate-reducing bacteria (SRB) and carbon dioxide (CO2) was investigated. The EIP was determined measuring the resistance of the emulsion water/crude oil, and the Wettability was determined measuring the resistance by the spreading method. Corrosiveness experiments of aqueous phase were carried out in a Rotating Cage Apparatus. During the experiments the pH, planktonic bacterial count, and concentrations of sulphide, sulphate, iron, calcium and magnesium ions in the solution were measured. After the experiment, sessile bacterial count and mass loss of carbon steel was determined; corrosion products on the metal surface were identified using X-ray diffraction, and corrosion morphology was determined using a scanning electron microscope, optical microscope and laser profilometer. The experimental results show that the crude oil evaluated has a 50% EIP, a Mixed-Wet Wettability and is an Inhibitive Hydrocarbon because reduced de corrosion rate in 30% |
| Disciplinas: | Ingeniería |
| Palabras clave: | Ingeniería petrolera, Oleoductos, Corrosión, Emulsión aceite-agua, Punto de inversión, Acero, Humectabilidad, Bacterias sulfato reductoras |
| Keyword: | Engineering, Petroleum engineering, Oil pipelines, Corrosion, Crude oil-water emulsion, Inversion point, Steel, Wettability, Sulphate-reducing bacteria |