| Revista: | Respuestas |
| Base de datos: | PERIÓDICA |
| Número de sistema: | 000420815 |
| ISSN: | 2422-5053 |
| Autores: | Raba Páez, Angela Mercedes1 Falcony Guajardo, Ciro2 |
| Instituciones: | 1Universidad Francisco de Paula Santander, Departamento de Física, Cúcuta, Norte de Santander. Colombia 2Instituto Politécnico Nacional, Centro de Investigación y de Estudios Avanzados, Ciudad de México. México 3Universidad Nacional de Colombia, Departamento de Física, Bogotá. Colombia |
| Año: | 2016 |
| Periodo: | Jul-Dic |
| Volumen: | 21 |
| Número: | 2 |
| Paginación: | 80-91 |
| País: | Colombia |
| Idioma: | Español |
| Tipo de documento: | Artículo |
| Enfoque: | Aplicado, descriptivo |
| Resumen en español | La fase T del pentóxido de niobio (Nb₂O₅) absorbe energía en la región del ultravioleta lo que lo hace un material promisorio en aplicaciones fotocatalíticas.Objetivo: En este trabajo se sintetizó, caracterizó y evaluó la actividad fotocatalítica, en la degradación de Rodamina B, del T-Nb2O5. Metodología: Las muestras fueron preparadas por el método sol-gel siguiendo dos procedimientos diferentes (NH4OH y H2O); los materiales fueron sinterizados a temperaturas de 650 °C y 750 °C y caracterizados por DRX, MEB y espectroscopias IR e UV-vis. Resultados: El NH4OH modifica el tamaño cristalino, la energía de banda gap y la porosidad del T-Nb2O5, además inhibe el crecimiento de nanopartículas de Nb2O5 en el proceso sol-gel, por lo tanto se ve modificada la cinética para la degradación de Rodamina B. La actividad fotocatalítica de las nanoestructuras es dominantemente determinada por el equilibrio de absorción y la cinética de la reacción. Conclusión: Los resultados de caracterización estructural, morfológica, vibracional y óptica permiten inferir que se obtuvo la cristalización del T-Nb2O5 y que a 750 °C el material exhibió una mayor eficiencia en la actividad fotocatalítica |
| Resumen en inglés | T phase of Niobium pentoxide (Nb₂O₅) absorbs energy in the ultraviolet region which makes it a promissory material in photocatalytic applications. Objective: In this work the T-Nb2O5 was synthesized, characterized and its photocatalytic performance for degradation of Rhodamine B was evaluated. Methods: The samples were made by the sol-gel method following two different procedures (NH4OH and H2O); the materials were sintered at 650 °C and 750°C temperatures and later characterized by XRD, SEM, IR and UV-vis spectroscopy. Results: NH4OH modifies the T-Nb2O5 crystalline size, band-gap energy, and porosity, besides inhibiting the growth of Nb2O5 nanoparticles in sol-gel process, and therefore the kinetics for Rhodamine B degradation are modified. The photocatalytic activity of the nanostructures is dominantly determined by adsorption equilibrium and reaction kinetics. Conclusions: The results of structural, morphological, vibrational and optic characterization allow to conclude that the crystallization of T-Nb2O5 was achieved, and that the material treated at 750°C showed an increased efficiency in the photocatalytic activity |
| Resumen en portugués | A fase T do pentóxido de nióbio (Nb₂O₅) absorve energia na região do ultravioleta tornando-se um material promissor para aplicações catalíticas. Objectivo:Neste estudo foi sintetizado, caracterizar e avaliar a actividade fotocatalítica na degradação de Rodamina B, o T-Nb2O5. Metodologia: As amostras foram preparadas pelo método de sol-gel, seguindo dois procedimentos diferentes: (NH4OH e H2O). Finalmente as amostras foram sinterizados a temperaturas de 650 °C e 750 °C para logo ser caracterizadas por: DRX, SEM e espectroscopia de IV e UV-VIS. Resultados: O uso do NH4OH modifica o tamanho dos cristalitos, a energia da banda e a porosidade do T-Nb2O5, também inibe o crescimento de nanopartículas Nb2O5 no processo sol-gel, por conseguinte, a cinética de degradação de Rodamina B. A é modificado. Conclusão: Os resultados da caracterização estrutural, morfológica, vibracional e óptico permitem inferir que foi obtido a cristalização da T-Nb2O5. Assim, as amostra em 750 °C apresentam uma maior eficiência na actividade fotocatalítica |
| Disciplinas: | Ingeniería |
| Palabras clave: | Ingeniería química, Catalizadores, Fotocatálisis, Pentóxido de niobio, Sol-gel |
| Keyword: | Chemical engineering, Catalysts, Photocatalysis, Niobium pentoxide, Sol-gel |