| Revista: | Materials research |
| Base de datos: | PERIÓDICA |
| Número de sistema: | 000312926 |
| ISSN: | 1516-1439 |
| Autores: | Teixeira, Ana Maria Rangel de Figueiredo1 Ogasawara, Tsuneharu2 Nobrega, Maria Cecília de Souza |
| Instituciones: | 1Universidade Federal Fluminense, Departamento de Quimica Analitica, Niteroi, Rio de Janeiro. Brasil 2Universidade Federal do Rio de Janeiro, Instituto Alberto Luiz Coimbra de Pos-Graduacao e Pesquisa de Engenharia, Rio de Janeiro. Brasil |
| Año: | 2006 |
| Periodo: | Jul-Sep |
| Volumen: | 9 |
| Número: | 3 |
| Paginación: | 257-262 |
| País: | Brasil |
| Idioma: | Inglés |
| Tipo de documento: | Nota breve o noticia |
| Enfoque: | Experimental |
| Resumen en inglés | The magnetic properties of sintered samples of cobalt-zinc ferrites produced from the corresponding coprecipitate were calculated based on hysteresis curves (Hc). The Hc values confirmed that soft ferrites were obtained by the procedure. A possible relation between the magnetic hysteresis curves and the microstructure of the sintered samples was investigated. X ray diffraction, thermal analysis and scanning electron microscopy were used to characterize the microstructure and the phases present in the sintered ceramic pieces, as well as those of their coprecipitated tri-metallic hydroxide precursor powders. It was found that sintering of Co0.5Zn0.5Fe2O4 at 1400 °C led to "honeycombing" of the ferrite grains and that there was no single phase in the microstructure of a sample sintered at 1400 °C. Thus, a more complete study was made of the behavior of the microstructure at lower sintering temperatures, i.e., in the 1100-1350 °C range |
| Disciplinas: | Ingeniería, Química |
| Palabras clave: | Ingeniería de materiales, Ingeniería metalúrgica, Química industrial, Ferritas, Sinterización, Tratamiento térmico, Cobalto, Zinc, Microestructuras |
| Keyword: | Engineering, Chemistry, Materials engineering, Metallurgical engineering, Industrial chemistry, Ferrites, Sintering, Thermal treatment, Cobalt, Zinc, Microstructures |
| Texto completo: | Texto completo (Ver HTML) |