| Revista: | Madera y bosques |
| Base de datos: | PERIÓDICA |
| Número de sistema: | 000453343 |
| ISSN: | 1405-0471 |
| Autores: | Zanatta, Paula1 Mattoso, Taline2 Gallio, Ezequiel2 Lazarotto, Marília2 Gatto, Darci Alberto2 Cunha, Alexsandro Bayestorff da1 Beltrame, Rafael2 |
| Instituciones: | 1Universidade do Estado de Santa Catarina, Centro de Ciencias Agroveterinarias, Lages, Santa Catarina. Brasil 2Universidade Federal de Pelotas, Centro de Engenharias, Pelotas, Rio Grande do Sul. Brasil |
| Año: | 2022 |
| Volumen: | 28 |
| Número: | 1 |
| País: | México |
| Idioma: | Inglés |
| Tipo de documento: | Artículo |
| Enfoque: | Experimental, analítico |
| Resumen en español | Se impregnó dióxido de titanio comercial en la madera de Pinus elliottii, con el objetivo de aumentar su durabilidad contra el ataque del hongo pardo de la Postia placenta y la fotodegradación causada por la radiación ultravioleta. Las muestras se pusieron a una presión de 8 bar durante 3 horas a diferentes concentraciones de TiO2 (0.5%, 0.25%, 0.124% y 0% de control). Para evaluar el efecto del hongo en la madera, la prueba se realizó de acuerdo con la norma ASTM D2017-05 y UNE-EN 113:1996 con modificaciones. La fotodegradación se realizó exponiendo una sección tangencial a radiación ultravioleta durante 400 horas, y los parámetros colorimétricos se evaluaron periódicamente. Estadísticamente, los tratamientos con TiO2 no diferían entre sí, pero eran mucho más bajos que el control, mostrando la efectividad de este producto en la protección de la madera contra los ataques de los degradadores. En cuanto a la fotodegradación, la madera tratada se mantuvo prácticamente sin cambios, a diferencia del control que tuvo un oscurecimiento acelerado principalmente en las primeras 50 horas. Con esta información, se puede afirmar que la madera tratada con TiO2 puede dificultar el acceso del hongo a la pared celular, inhibir su crecimiento y crear una barrera que protege a los polímeros de la fotodegradación, aumentando su durabilidad y emergiendo como una alternativa potencial para tratamiento de la madera |
| Resumen en inglés | It was impregnated commercial titanium dioxide into Pinus elliottii wood, aiming to increase its durability against the attack of brown rot fungus Postia placenta and photodegradation caused by ultraviolet radiation. The samples were put under 8 bar pressure for 3 hours at different concentrations of TiO2 (0.5%, 0.25%, 0.124% and 0%-control). To evaluate the effect of the fungus on the wood, the test was carried out according to ASTM D2017-05 and UNE-EN 113:1996 with modifications. The photodegradation was performed by exposing a tangential section to ultraviolet radiation for 400 hours, and the colorimetric parameters were periodically evaluated. Statistically, the treatments with TiO2 did not differ among themselves, but were much lower than the control, showing the effectiveness of this product in protecting the wood against the attacks of degraders. As for the photodegradation, the treated wood remained practically unchanged, differently from the control that had a darkening accelerated mainly in the first 50 hours. With this information, it can be stated that TiO2 treated wood is able to hinder the fungus access to the cell wall, to inhibit its growth and to create a barrier that protects the polymers from photodegradation, increasing its durability and emerging as a potential alternative for wood treatment |
| Disciplinas: | Agrociencias, Biología |
| Palabras clave: | Silvicultura, Fitopatología, Hongos, Postia placenta, Pinus elliottii, Dióxido de titanio, Radiación ultravioleta, Tecnología de la madera |
| Keyword: | Silviculture, Phytopathology, Fungi, Postia placenta, Pinus elliottii, Titanium dioxide, Ultraviolet radiation, Wood technology |
| Texto completo: | Texto completo (Ver HTML) Texto completo (Ver PDF) |