| Revista: | Facultad de Ingeniería - Universidad Pedagógica y Tecnológica de Colombia |
| Base de datos: | PERIÓDICA |
| Número de sistema: | 000441679 |
| ISSN: | 0121-1129 |
| Autores: | Aragón Lozano, Walter Yesid1 Fernández Vega, Luis Felipe1 Higuera Cobos, Oscar Fabián1 Tristancho Reyes, José Luis2 Pedraza Yepes, Cristian Antonio1 |
| Instituciones: | 1Universidad del Atlántico, Barranquilla, Atlántico. Colombia 2Universidad Tecnológica de Pereira, Pereira, Risaralda. Colombia |
| Año: | 2020 |
| Periodo: | Ene-Mar |
| Volumen: | 29 |
| Número: | 54 |
| País: | Colombia |
| Idioma: | Español |
| Tipo de documento: | Artículo |
| Enfoque: | Experimental, aplicado |
| Resumen en español | En esta investigación, muestras de acero AISI 316L fueron sometidas a deformación plástica severa por la técnica presión calibrada (GP) mediante el uso de 2 matrices de acero de herramientas tipo A2 con dimensiones de 96 mm X 96 mm, una matriz corrugada con dientes de 2 mm y ángulo de 45° y una matriz plana. Cada pase por la matriz GP incluye 2 estados de corrugado y 2 estados de enderezado con una rotación de 180° entre cada uno de ellos. Esta configuración provee al material una deformación teórica equivalente por pase de ε~1.16. Al material fue deformado por 4 pases por GP hasta una deformación equivalente de ε~4,64. Previo a la deformación, las probetas fueron sometidas a un tratamiento térmico de recocido durante una 1 hora a 1000 °C con enfriamiento en agua, con el fin de eliminar la textura de laminación. El material en estado de recocido y deformado se caracterizó química y microestructuralmente mediante fluorescencia de rayos X y microscopía electrónica de barrido, respectivamente. Con el fin de evaluar el comportamiento a la corrosión del material, se utilizó la resistencia a la polarización lineal y el análisis mediante las curvas de Tafel en una solución de 0,6 M de NaCl por un tiempo de 0 y 24 horas. Los resultados muestran un comportamiento atípico en cuanto a la resistencia a la corrosión del acero AISI 316L. Se observó un aumento en la resistencia a la corrosión del 45% del material después de 4 pases por GP en comparación con el material recocido (0 pases) |
| Resumen en inglés | In this investigation, samples of AISI 316L steel were subjected to severe plastic deformation by the groove pressing (GP) technique using 2 dies A2 type tool steel dies with dimensions of 96 mm X 96 mm, a corrugated die with 2 mm teeth and 45° angle and a flat die. Each pass through the GP die includes 2 states of corrugated and 2 states of straightening with a 180° rotation between each of them. This configuration provides the material with an equivalent theoretical deformation per pass of ε~1.16. The material was deformed by 4 passes per GP to an equivalent deformation of ε~4.64. Prior to the deformation, the specimens were subjected to an annealing heat treatment for 1 hour at 1000 °C with water cooling, in order to eliminate the lamination texture. The annealed and deformed material was characterized chemically and microstructurally by X-ray fluorescence and scanning electron microscopy, respectively. In order to evaluate the corrosion behavior of the material, linear polarization resistance and analysis by Tafel plot were used in a 0.6 M NaCl solution for 0 and 24 hours. The results show an atypical behavior regarding the corrosion resistance of AISI 316L steel. An increase in corrosion resistance of 45% of the material was observed after 4 passes per GP compared to annealed material (0 passes) |
| Resumen en portugués | Nesta pesquisa, amostras de aço AISI 316L foram submetidas a deformação plástica severa pela técnica pressão calibrada (GP) mediante o uso de 2 matrizes de aço de ferramentas tipo A2 com dimensões de 96 mm X 96 mm, uma matriz corrugada com dentes de 2 mm e ângulo de 45° e uma matriz plana. Cada passe pela matriz GP inclui 2 estados de corrugado e 2 estados de endireitado com uma rotação de 180° entre cada um deles. Esta configuração provê ao material uma deformação teórica equivalente por passe de ε~1.16. O material foi deformado por 4 passes por GP até uma deformação equivalente de ε~4,64. Prévio à deformação, as provetas foram submetidas a um tratamento térmico de recozimento durante uma 1 hora a 1000 °C com esfriamento em água, com o fim de eliminar a textura de laminação. O material em estado de recozimento e deformado caracterizou-se química e microestruturalmente mediante fluorescência de raios X e microscopia eletrônica de varredura, respectivamente. Com o fim de avaliar o comportamento à corrosão do material, utilizou-se a resistência à polarização linear e a análise mediante as curvas de Tafel em uma solução de 0,6 M de NaCl por um tempo de 0 e 24 horas. Os resultados mostram um comportamento atípico em quanto à resistência à corrosão do aço AISI 316L. Observou-se um aumento na resistência à corrosão de 45% do material depois de 4 passes por GP em comparação com o material recozido (0 passes) |
| Disciplinas: | Ingeniería |
| Palabras clave: | Ingeniería metalúrgica, Acero inoxidable austenítico, Curvas de Tafel, Deformación plástica severa, Presión calibrada, Resistencia a la polarización lineal, Velocidad de corrosión |
| Keyword: | Metallurgical engineering, Austenitic stainless steel, Corrosion rate, Groove pressing, Linear polarization resistance, Severe plastic deformation, Tafel plot |