| Revista: | Ceramica industrial |
| Base de datos: | PERIÓDICA |
| Número de sistema: | 000428056 |
| ISSN: | 0366-6913 |
| Autores: | Silva, R.S1 Antonelli, E1 Hernandes, A.C1 |
| Instituciones: | 1Universidade de Sao Paulo, Instituto de Física de Sao Carlos, Sao Carlos, Sao Paulo. Brasil |
| Año: | 2006 |
| Periodo: | Jul-Sep |
| Volumen: | 52 |
| Número: | 323 |
| Paginación: | 168-173 |
| País: | Brasil |
| Idioma: | Portugués |
| Tipo de documento: | Artículo |
| Enfoque: | Experimental |
| Resumen en inglés | Barium calcium titanate nanopowders (Ba1-xCaxTiO3: x = 0.05, 0.10, 0.15 and 0.23 mol%) have been synthesized at relative low temperature ( 800 ºC) through the modified polymeric precursor method. High relative density ceramics (> 97%) and microstructure with homogeneous grain size were obtained at relative low temperature and time of sintering (1275 °C/1 h). It was also observed that the crystallite size of the calcined powder and the average grain size of the sintered ceramics decrease with the increase of the calcium concentration |
| Resumen en portugués | Pós nanométricos de titanato de bário e cálcio (Ba1-xCaxTiO3: x = 0,05/0,10/0,15/0,23 mol%) foram sintetizados a temperaturas relativamente baixas (800 °C) por meio do método de precursores poliméricos modificado. Corpos cerâmicos foram obtidos com alta densidade relativa (> 97%) e microestrutura com tamanho de grãos homogêneos, a temperatura e tempo de sinterização relativamente baixos (1275 °C/1 h). Observamos também que o tamanho de cristalitos no pó calcinado e o tamanho médio de grãos nos corpos cerâmicos sinterizados diminuem com o aumento da concentração de Ca |
| Disciplinas: | Química, Ingeniería |
| Palabras clave: | Química inorgánica, Ingeniería de materiales, Polvos, BaTiO3, Sinterización |
| Keyword: | Inorganic chemistry, Materials engineering, Powders, BaTiO3, Sintering |
| Texto completo: | Texto completo (Ver PDF) |