Revista: | Revista mexicana de física |
Base de datos: | PERIÓDICA |
Número de sistema: | 000426087 |
ISSN: | 0035-001X |
Autors: | Quiroz, A1 Abatal, M1 Chavira, E2 García Vázquez, V3 Marinero, E4 Nishioka, M5 |
Institucions: | 1Universidad Autónoma del Carmen, Facultad de Ingeniería, Ciudad del Carmen, Campeche. México 2Universidad Nacional Autónoma de México, Instituto de Investigaciones en Materiales, Ciudad de México. México 3Benemérita Universidad Autónoma de Puebla, Instituto de Física, Puebla. México 4Purdue University, West Lafayette, Indiana. Estados Unidos de América 5Hitachi San Jose Research Center, San José, California. Estados Unidos de América |
Any: | 2018 |
Període: | May-Jun |
Volum: | 64 |
Número: | 3 |
País: | México |
Idioma: | Inglés |
Tipo de documento: | Artículo |
Enfoque: | Analítico, teórico |
Resumen en inglés | We report the Ca0.90Sr0.10RuO3 compound synthesized by solid-state reaction method at ambient pressure using temperatures between 700 and 800 C in air. By X-ray powder diffraction (XRD), we determine a solid solution until Ca0.85Sr0.15RuO3 compound. Scanning electron microscopy (SEM) indicates than the particle size varies between 0.422 and 1.598 μm. The resistance measurement, as a function of temperature measurement from 10 to 300 K for Ca0.90Sr0.10RuO3 compound shows a metallic behavior. Finally, photoluminescence (PL) and its temperature dependence of Ca0.90Sr0.10RuO3 compound in the temperature range 6.7-296 K were measured. It was observed than the main broad band centered at ∼ 1.73 eV with the shoulders at ∼ 1.38 eV and ∼ 2.05 eV exists in the entire temperature range. It can be well fitted by three Gaussian curves B1, B2 and B3, centered at ∼ 1.38, ∼ 1.73 and ∼ 2.05 eV, respectively. The transitions identified as B1 and B2 are studied with temperature. The photoluminescence mechanics for Ca0.90Sr0.10RuO3 compound are presented based on the electronic structures formed by the interactions among spin, charge and lattice, in which B1 was identified with the charge transfer excitation of an electron from the lower Jahn-Teller split eg level of a Ru3+ ion to the eg level of an adjacent Ru4+ ion, B2 was assigned to the transition between the spin up and spin down eg bands separated by Hund’s coupling energy Ej , whereas B3 is attributed to the transition, determined by the crystal field energy Ec between a t2g core electron of Ru3+ to the spin up eg bands of Ru4+ by a dipole allowed charge transfer process |
Disciplines | Física y astronomía |
Paraules clau: | Física, Difracción de rayos X, Rutenos, Fotoluminiscencia, Magnetoresistencia colosal |
Keyword: | Physics, X-ray diffraction, Ruthenates, Photoluminescence, Colossal magnetoresistance |
Text complet: | Texto completo (Ver HTML) Texto completo (Ver PDF) |