| Revista: | Revista mexicana de física |
| Base de datos: | PERIÓDICA |
| Número de sistema: | 000336956 |
| ISSN: | 0035-001X |
| Autors: | Armendariz, V1 José Yacamán, Miguel3 Duarte Moller, A4 Peralta Videa, J.R1 Troiani, H3 Herrera, I1 Gardea Torresdey, J.L2 |
| Institucions: | 1University of Texas at El Paso, Department of Chemistry, El Paso, Texas. Estados Unidos de América 2University of Texas at El Paso, Environmental Science and Engineering Ph.D. Program, El Paso, Texas. Estados Unidos de América 3University of Texas at Austin, Department of Chemical Engineering, Austin, Texas. Estados Unidos de América 4Centro de Investigación en Materiales Avanzados S.C., Chihuahua. México |
| Any: | 2004 |
| Període: | Jun |
| Volum: | 50 |
| Paginació: | 7-11 |
| País: | México |
| Idioma: | Inglés |
| Tipo de documento: | Artículo |
| Enfoque: | Experimental |
| Resumen en español | En este estudio se presenta la bio-reducción de Au(III) a Au(0) por la biomasa de trigo y la formación de nanopartículas de oro. La biomasa de trigo fue lavada, molida y tamizada para incrementar el área de biomasa expuesta a la solución de Au. La biomasa de trigo fue reaccionada con una solución 0.3 mM de tetraclorourato de potasio a pH de 1, 2, 3, 4, 5 y 6 por un periodo de tres horas y media a temperatura ambiente. La biomasa fue analizada usando un microscopio JEOL-4000 EX de alta resolución para caracterizar el tamaño y forma de las nanoestructuras obtenidas. Las nanopartículas observadas fueron: Fcc tetraedral (T), decaedral (Dh), Hexagonal (He), Icosaedral “multitwinned” (I), forma irregular (IRR), y nanopartículas con forma de columnas. El mayor porcentaje de nanopartículas obtenidas fueron aquellas de 10-30 nm de diámetro |
| Resumen en inglés | In this study, the bio-reduction of Au(III) to Au(0) by wheat biomass and the subsequent production of gold nanoparticles of various shapes and sizes is presented. The dry biomass was ground and sieved in order to assure a uniform particle size and having more area of biomass exposed to the gold. Wheat biomass was exposed to a 0.3mM potassium tetrachloroaurate solution at pH values of 2, 3, 4, 5, and 6 for three and a half hours at room temperature. After that time, the biomass pellets were analyzed using a high resolution transmission electron microscope, JEOL-4000 EX, in order to characterize the gold nanoparticles. The results showed that wheat biomass produced nanostructures of the following morphologies: Fcc tetrahedral (T), decahedral (Dh), hexagonal (He), icosahedral multitwinned (I), irregular shape (Irr), and rod shape nanoparticles. The highest percent of the nanoparticles formed had a particle size ranging from 10-30 nm |
| Disciplines | Física y astronomía, Química |
| Paraules clau: | Física, Fisicoquímica y química teórica, Oro, Nanopartículas |
| Keyword: | Physics and astronomy, Chemistry, Physics, Physical and theoretical chemistry, Ecology, Gold, Nanoparticles |
| Text complet: | Texto completo (Ver PDF) |