Revista: | Polimeros (Sao Carlos) |
Base de datos: | PERIÓDICA |
Número de sistema: | 000314085 |
ISSN: | 1678-5169 |
Autors: | Palmer, Guillermo1 Demarquette, Nicole R |
Institucions: | 1Universidade de Sao Paulo, Escola Politecnica, Sao Paulo. Brasil |
Any: | 2003 |
Període: | Ene-Mar |
Volum: | 13 |
Número: | 1 |
Paginació: | 72-78 |
País: | Brasil |
Idioma: | Portugués |
Tipo de documento: | Artículo |
Enfoque: | Experimental, analítico |
Resumen en inglés | Interfacial tension between molten polymers is a key factor that helps predicting the morphology of polymer blends. In this work, the theories of Tomotika and Tjahjadi et al. to measure interfacial tension between molten polymers using the breaking thread method are evaluated and compared. In particular, both theories were tested for PP/PS polymer pair at temperature of 200 °C. The average values of interfacial tension calculated using Tomotika´s theory and Tjahjadi et al.´s theory are 5.88 mN/m and 5.66 mN/m, respectively |
Resumen en portugués | A tensão interfacial entre polímeros fundidos é um fator chave para a predição da morfologia de blendas poliméricas. Neste trabalho, as teorias de Tomotika e Tjahjadi et al. para medir tensão interfacial entre polímeros fundidos usando o método de fibra quebrante são avaliadas e comparadas. Em particular, foram testadas ambas as teorias para o par de polímeros PP/PS à temperatura de 200 °C. O valor médio de tensão interfacial calculado usando a teoria de Tomotika foi de 5,88 mN/m, e usando a teoria de Tjahjadi et al. foi de 5,66 mN/m |
Disciplines | Ingeniería |
Paraules clau: | Ingeniería de materiales, Ingeniería metalúrgica, Mezcla de polímeros, Tensión interfacial, Morfología, Reología |
Keyword: | Engineering, Materials engineering, Metallurgical engineering, Polymers blend, Interfacial tension, Morphology, Rheology |