| Revista: | Interciencia |
| Base de datos: | PERIÓDICA |
| Número de sistema: | 000440848 |
| ISSN: | 0378-1844 |
| Autors: | Méndez Serrano, Jorge Velázquez Enríquez, Ulises1 Contreras Bulnes, Rosalía1 De La Rosa Gómez, Isaías2 Sawada, Toshiko3 Yamaguchi, Ryozo3 |
| Institucions: | 1Universidad Autónoma del Estado de México, Facultad de Odontología, Toluca, Estado de México. México 2Instituto Tecnológico de Toluca, Toluca, Estado de México. México 3Asahi University, Mizuho, Gifu. Japón |
| Any: | 2020 |
| Volum: | 45 |
| Número: | 1 |
| Paginació: | 23-27 |
| País: | Venezuela |
| Idioma: | Inglés |
| Tipo de documento: | Artículo |
| Enfoque: | Experimental, aplicado |
| Resumen en español | Este estudio in vitro evaluó la adhesión bacteriana de C. albicans (ATCC18804) y S. mutans (ATCC25175) de manera independiente en bloques de polimetilmetacrilato (PMMA) modificados con nanopartículas de plata (AgNPs). Se usó un total de 160 muestras clasificadas en ocho grupos. C. albicans y S. mutans fueron cultivados independientemente. Los bloques fueron sumergidos en una solución conteniendo microorganismos radiomarcados con tritio (3 H). Para el análisis cuantitativo el marcador radiactivo 3 H fue usado para codificar las colonias bacterianas adheridas a la superficie de los materiales proporcionalmente a la colonización a 37°C. En el análisis estadístico se utilizó análisis de varianza (Sheffè post-hoc). Se encontraron diferencias estadísticamente significativas en la adhesión bacteriana entre los grupos de PMMA modificados con AgNPs. Los grupos de PMMA termocurables demostraron baja adherencia a C. albicans comparados con los grupos de PMMA autocurables Los grupos de PMMA termocurable resultaron resistentes a la adhesión bacteriana sin importar su modificación con AgNPs |
| Resumen en inglés | This in vitro study independently evaluated the adhesion of Candida albicans (ATCC 18804) and Streptococcus mutans (ATCC 25175) to polymethylmethacrylate (PMMA) blocks modified with silver nanoparticles (AgNPs). A total of 160 samples were used, separated into eight groups. S. mutans and C. albicans were independently cultivated. The blocks were submerged in a solution containing microorganisms radiolabeled with tritium (3 H). For quantitative analysis, the radioactive marker 3 H was used to identify the bacteria that adhered to the surface of the materials previous to colonization at 37°C. Analysis of variance (Sheffè post hoc) was used for statistical analysis. Significant differences in microbial adhesion were found among the groups of AgNP-modified PMMA. Heat-curing PMMA showed lower adhesion to C. albicans relative to self-curing PMMA. Heat-curing PMMA with AgNPs showed the greatest levels of adhesion to S. mutans and C. albicans, respectively, similar to those of self-curing PMMA without AgNPs. The groups of heat-curing PMMA were more resistant to bacterial adhesion in spite of the modification with AgNPs |
| Resumen en portugués | Este estudo in vitro avaliou a adesão bacteriana de C. Albicans (ATCC18804) e S. Mutans (ATCC25175) de maneira independente em blocos de polimetilmetacrilato (PMMA) modificados com nanopartículas de prata (AgNPs). Foi utilizado um total de 160 amostras classificadas em oito grupos. C. Albicans y S. mutans foram cultivados independentemente. Os blocos foram submergidos em uma solução contendo microrganismos radiomarcados com trítio (3 H). Para a análise quantitativa foi utilizado o marcador radiativo 3 H para codificar as colônias bacterianas aderidas na superfície dos materiais proporcionalmente à colonização a 37°C. No estudo estatístico foi utilizada análise de variância (Sheffè post-hoc). Encontraram-se diferenças estatisticamente significativas na adesão bacteriana entre os grupos de PMMA modificados com AgNPs. Os grupos de PMMA termocuráveis demostraram baixa aderência a C. albicans comparados com os grupos de PMMA autocuráveis. Os grupos de PMMA termocurável resultaram resistentes à adesão bacteriana sem importar sua modificação com AgNPs |
| Disciplines | Medicina |
| Paraules clau: | Microbiología, Odontología, Bacterias, Cavidad oral, Adhesión bacteriana, Materiales dentales, Radioisótopos, Candida albicans, Streptococcus mutans |
| Keyword: | Microbiology, Dentistry, Bacteria, Oral cavity, Bacterial adhesion, Dental materials, Radioisotopes, Candida albicans, Streptococcus mutans |
| Text complet: | https://www.interciencia.net/wp-content/uploads/2020/02/23_6625_Com_Velazquez_v45n1.pdf |