| Resumen en español | Se reporta la síntesis y la caracterización de manganitas de Lα 0.67-x Pr x Cα 0.33 Mn0 3 con0.13 ≤ x ≤ 0.67, obtenidas por reacción de estado sólido, y de LαMn 1-x Ni x 0 3 , con 0.0 ≤ x ≤ 0.5, obtenidas por el método sol-gel. Las manganitas se caracterizaron a través de medidas difracción de rayos X, resistividad eléctrica y susceptibilidad magnética en función de la temperatura. Se concluyó que los esfuerzos de tensión y compresión en la red dependen fuertemente del contenido de, Pr, Co y Ni en las muestras, y que las temperaturas de transición de las fases metal-aislante y ferromagnética-paramagnética depende fuertemente dichos esfuerzos: a mayor contenido de Pr se produjo mayores esfuerzos de tensión que desplazaron el corrimiento de la transición ferromagnética-paramagnética a temperaturas más bajas, mientras que a mayor contenido de Ni y Co se produjo mayores esfuerzos de comprensión que desplazaron el corrimiento de las transiciones metal-aislante y ferromagnética-paramagnética a temperaturas más altas. |
| Resumen en inglés | This paper presents the results obtained from the synthesis and morphological characterization of different magnetite samples: Lα 0.67-x Pr x Cα 0.33 Mn0 3 at 0.13 ≤ x ≤ 0.67 produced by a solid-state reaction mechanism and LαMn 1-x Ni x 0 3 at 0.0 ≤ x ≤ 0.5 produced by the sol-gel method. These samples were characterized using X-ray diffraction spectroscopy and by measuring electric resistivity and magnetic susceptibility which were carried out as a function of temperature. Notably, the effects of strain and compressive strength on the lattices of magnetite samples were highly dependent on the concentration of Pr, Co and Ni. Moreover, the transition temperatures of metal-insulator and ferromagnetic-paramagnetic phases also largely depend on these strength effects, e.g., at higher concentrations of Pr, effects of increased strain strength were observed, relocating the shifts of ferromagnetic-paramagnetic transitions to lower temperatures. On the other hand, effects of increased compressive strength were observed at higher concentrations of Ni and Co, relocating the shifts of ferromagnetic-paramagnetic and metal-insulator transitions to higher temperatures. |
| Paraules clau: | Manganitas, Esfuerzos de tensión, Esfuerzos de compresión, Temperatura de Curie, Temperatura de transición |
| Keyword: | Magnetite, Strain strength, Curie temperature, Transition temperature |