| Revista: | Concreto y cemento. Investigación y desarrollo |
| Base de datos: | PERIÓDICA |
| Número de sistema: | 000353002 |
| ISSN: | 2007-3011 |
| Autores: | Helene, Paulo Roberto Do Lago1 Castro Borges, Pedro2 |
| Instituciones: | 1Universidade de Sao Paulo, Escola Politecnica, Sao Paulo. Brasil 2Instituto Politécnico Nacional, Centro de Investigación y de Estudios Avanzados, Mérida, Yucatán. México |
| Año: | 2009 |
| Volumen: | 1 |
| Número: | 1 |
| Paginación: | 25-35 |
| País: | México |
| Idioma: | Inglés |
| Tipo de documento: | Artículo |
| Enfoque: | Aplicado, descriptivo |
| Resumen en español | Si bien las causas, mecanismos y factores que promueven la carbonatación del concreto han sido ampliamente estudiadas, los factores a considerar durante la fabricación de concreto, tales como las combinaciones en la proporción de la mezcla – que es un factor que influye en la tasa de carbonatación - no han sido investigados ni modelados adecuadamente. El presente trabajo abarcó la elaboración de muestras de concreto con diferentes asentamientos, contenido de cemento y diversas proporciones de agua / cemento, muestras que fueron sometidas a pruebas de carbonatación acelerada. Como ya se informó en estudios previos, la mayor influencia en la tasa de carbonatación del concreto la tuvo la proporción agua / cemento. El contenido de cemento no influyó en la tasa de carbonatación cuando la proporción agua / cemento se mantuvo constante; sin embargo, si la trabajabilidad se mantenía constante, el incremento en el contenido de cemento dio lugar a una reducción de la profundidad de carbonatación. Mediante la realización de este experimento, el principal objetivo del presente estudio fue demostrar cómo un nomograma de diseño de mezcla, además de ser una herramienta poderosa para el profesional, puede servir en la predicción y reducción del grado de carbonatación del concreto, mediante la identificación de los parámetros más adecuados para la mezcla |
| Resumen en inglés | Although the causes, mechanisms, and factors which promote concrete carbonation have been widely studied, factors that come into play during concrete fabrication such as mix proportioning combinations — a critical factor influencing the rate of carbonation — have not been properly researched or modeled. The present work involved the fabrication of concrete samples with different slumps, cement contents, and water/cement ratios which were subjected to tests of accelerated carbonation. As reported in previous studies, the water/cement ratio had the greatest influence on concrete carbonation rates. Cement content did not influence the carbonation rate when the water/cement ratio was kept constant; however, if the workability was fixed, an increase in cement content led to a reduction in carbonation depth. By conducting this experiment, the main objective of the present study was to demonstrate how a mix design nomogram, a side from being a powerful tool for the practitioner, can serve to predict and reduce the degree of concrete carbonation by identifying the most appropriate mixture parameters |
| Resumen en portugués | Embora as causas, mecanismos e fatores que promovem a carbonatação do concreto têm sido amplamente estudados, os fatores a considerar durante o fabrico do concreto, tais como as combinações da mistura – fator crítico que tem influência na taxa de carbonatação – ainda não foram adequadamente nem pesquisados, nem modelados. O presente trabalho abrangeu o fabrico de amostras de concreto, com diferentes assentamentos, conteúdo de cimento e diferentes proporções d’água / cimento, e essas amostras foram submetidas a testes de carbonatação acelerada. Como já foi exposto em estudos prévios, a maior influência na taxa de carbonatação do concreto tem sido dada pela proporção água / cimento. O teor de cimento não influenciou na taxa de carbonatação quando a proporção água / cimento foi mantida constante, porém, se a trabalhabilidade foi fixada, um acréscimo no teor de cimento levou para uma redução na profundidade da carbonatação. Ao realizar esta experiência, o principal objetivo deste estudo era demonstrar que um nomograma de desenho de misturas, além de ser uma ferramenta poderosa para o profissional, pode auxiliar para predizer e reduzir o grau de carbonatação do concreto, através da identificação daqueles parâmetros da mistura que sejam os mais adequados |
| Disciplinas: | Ingeniería |
| Palabras clave: | Ingeniería civil, Ingeniería de materiales, Concreto, Proporcion de mezcla, Contenido de agua, Carbonatación, Corrosión, Durabilidad |
| Keyword: | Engineering, Civil engineering, Materials engineering, Concrete, Mixture ratio, Water content, Carbonation, Corrosion, Durability |
| Texto completo: | Texto completo (Ver PDF) |