Evaluation of inorganic and organic bone components after application of an apatite-coated Al2O3 implants as scaffolds for bone repair
Título del documento: Evaluation of inorganic and organic bone components after application of an apatite-coated Al2O3 implants as scaffolds for bone repair
Revista: Brazilian archives of biology and technology
Base de datos: PERIÓDICA
Número de sistema: 000373454
ISSN: 1516-8913
Autors: 1
2
3
3
Institucions: 1Faculdade Santo Agostinho, Laboratorio de Fisiologia, Teresina, Piaui. Brasil
2Faculdade Diferencial, Laboratorio de Anatomia, Teresina, Piaui. Brasil
3Universidade do Vale do Paraiba, Faculdade de Ciencias da Saude, Sao Jose dos Campos, Sao Paulo. Brasil
Any:
Període: May-Jun
Volum: 57
Número: 3
Paginació: 334-339
País: Brasil
Idioma: Inglés
Tipo de documento: Artículo
Enfoque: Analítico, descriptivo
Resumen en inglés The aim of this work was to study the influence of uncoated and apatite-coated Al2O3 implants on bone regeneration after 30 days of surgery in New Zealand white rabbits. Twelve samples of Al2O3 implants were prepared and half of them (n = 6) were apatite-coated by the modified biomimetic method. Three experimental groups were tested as Group C - control, surgery procedure without cerami c implant, Group Ce - uncoated Al 2O3 implants (n = 6) and Group CeHA - apatite-coated Al2O3 implants (n = 6). The mineralization of the Al2O3 implants was analyzed in bone fragments using FT-Raman spectroscopy. Raman peaks at 959 cm-1 and 2940 cm-1 evaluated the inorganic and organic bone content, respectively. In vivo citotoxicity was analyzed using micronucleus test. Inorganic and organic content were higher in CeHA samples than in Ce and C (CeHA > Ce > C). FT-Raman spectroscopy showed that the higher the deposition of the organic matrix, more mineralization occurred. The micronucleus test showed that the uncoated and apatite-coated Al2O3 implants were non-cytotoxic and safe to in vivo applications
Disciplines Medicina veterinaria y zootecnia
Paraules clau: Medicina veterinaria,
Regeneración ósea,
Espuma metálica,
Alúmina,
Apatita,
Conejos,
Prueba de micronúcleos,
Citotoxicidad
Keyword: Veterinary medicine and animal husbandry,
Veterinary medicine,
Bone regeneration,
Metallic foam,
Alumina,
Apatite,
Rabbits,
Micronucleus test,
Cytotoxicity
Text complet: Texto completo (Ver HTML)