| Revista: | Dyna (Medellín) |
| Base de datos: | PERIÓDICA |
| Número de sistema: | 000421976 |
| ISSN: | 0012-7353 |
| Autores: | Gómez Gómez, Adriana1 Vinasco Isaza, Luz Elena1 Lima, Nelson Batista de2 Tenorio, Jorge Aberto Soares3 |
| Instituciones: | 1Pontificia Universidad Javeriana, Departamento de Ingeniería Civil e Industrial, Cali, Valle del Cauca. Colombia 2Instituto de Pesquisas Energeticas e Nucleares, Departamento de Caracterizacao de Materiais, Sao Paulo. Brasil 3Universidade de Sao Paulo, Departamento de Engenharia Quimica, Sao Paulo. Brasil |
| Año: | 2018 |
| Periodo: | Sep |
| Volumen: | 85 |
| Número: | 206 |
| Paginación: | 348-354 |
| País: | Colombia |
| Idioma: | Español |
| Tipo de documento: | Artículo |
| Enfoque: | Aplicado, descriptivo |
| Resumen en español | En este trabajo se presenta la caracterización de una escoria de aluminio proveniente de la industria primaria, con tamaño de partícula inferior a 3.35 mm. Inicialmente el material fue separado en cuatro fracciones granulométricas las cuales fueron analizadas mediante difracción de rayos X con el fin de analizar la cantidad de cada una de las fases cristalinas presentes en la escoria. Se encontraron las siguientes fases: aluminio metálico, óxido de aluminio, espinelio, espinelio con defecto, diaoyudaoite y nitruro de aluminio. La dependencia del tamaño de partícula con la cantidad de cada una de las fases cristalinas fue analizada mediante un análisis de varianza (ANOVA) con un nivel de confianza del 99%. Del análisis estadístico se pudo concluir que la variación en el contenido encontrado de cada fase cristalina es explicada en un alto porcentaje por el tamaño de partícula |
| Resumen en inglés | The Rietveld method was used in order to determine the amount of crystalline phases present in aluminum dross with particle size less than 3.35 mm. Initially, the dross was separated in four granulometric fractions by screening. Two samples of each granulometric size were obtained by means of quartering and homogenization. Each sample was grounded and subsequently analyzed by X-ray diffraction in order to identify and quantify the crystalline phases present in the dross. Metallic aluminum, aluminum oxide, spinel, defect spinel, diaoyudaoite and aluminum nitride were identified and then quantified by the Rietveld method. In order to observe the dependence of the particle size with the amount of each phase, statistical analyses was done by means of analyses of variance (ANOVA). The coefficient of determination R2 was greater than 94% for all phases except for the NaAl11O17 phase. Thus, the amount of each crystalline phase is satisfactory explained by particle size |
| Disciplinas: | Ingeniería |
| Palabras clave: | Ingeniería civil, Ingeniería de materiales, Materiales de construcción, Escoria de aluminio, Caracterización química, Método de Rietveld |
| Keyword: | Civil engineering, Materials engineering, Construction materials, Aluminum dross, Chemical characterization, Rietveld method |
| Texto completo: | Texto completo (Ver HTML) |